公开(公告)号：US20070066477A1

公开(公告)日：2007-03-22

申请号：US11521683

申请日：2006-09-15

申请人： Brian Harper ,  Kenneth Hrdina ,  John LaSala

发明人： Brian Harper ,  Kenneth Hrdina ,  John LaSala

IPC分类号： C03B19/06 ,  C03C3/06 ,  C03B32/00

CPC分类号： C03C3/06 ,  C03B19/1453 ,  C03B32/00 ,  C03B2201/07 ,  C03B2201/075 ,  C03B2201/21 ,  C03B2201/23 ,  C03C2201/21 ,  C03C2201/23 ,  C03C2203/54 ,  G03F7/708 ,  Y10S501/905

摘要： Disclosed are methods for hydrogen loading silica glass and silica glass comprising loaded H2. The methods can lead to H2 gradient in the glass material. Alternatively, the method may involve the use of varying H2 partial pressure of H2 in the atmosphere. Both can result in expedited hydrogen loading process.

摘要翻译： 公开了用于氢气加载石英玻璃和包含加载H 2 N 2的二氧化硅玻璃的方法。 这些方法可导致玻璃材料中的H 2 2梯度。 或者，该方法可以涉及在气氛中使用H 2 H 2 H 2 H 2分压的变化。 两者都可以产生加速氢气加载过程。

公开(公告)号：US20060137397A1

公开(公告)日：2006-06-29

申请号：US11148504

申请日：2005-06-08

申请人： Dana Bookbinder ,  Richard Fiacco ,  Kenneth Hrdina ,  Lisa Moore ,  Susan Schiefelbein

发明人： Dana Bookbinder ,  Richard Fiacco ,  Kenneth Hrdina ,  Lisa Moore ,  Susan Schiefelbein

IPC分类号： C03B20/00 ,  C03C3/06

CPC分类号： C03C3/06 ,  C03B19/1453 ,  C03B19/1469 ,  C03B2201/03 ,  C03B2201/04 ,  C03B2201/07 ,  C03B2201/075 ,  C03B2201/21 ,  C03B2201/23 ,  C03C2201/11 ,  C03C2201/21 ,  C03C2201/23 ,  C03C2203/40 ,  C03C2203/54 ,  G03F7/70958

摘要： Disclosed are high purity synthetic silica material having an internal transmission at 193 nm of at least 99.65%/cm and method of preparing such material. The material is also featured by a high compositional homogeneity in a plane transverse to the intended optical axis. The soot-to-glass process for making the material includes a step of consolidating the soot preform in the presence of H2O and/or O2.

摘要翻译： 公开了具有193nm以上的内透射率为至少99.65％/ cm 3的高纯度合成二氧化硅材料及其制备方法。 该材料的特征还在于横向于预期光轴的平面中具有高的组成均匀性。 用于制造材料的烟灰对玻璃工艺包括在H 2 O 2和/或O 2 2的存在下固化烟灰预制件的步骤。

公开(公告)号：US20070004579A1

公开(公告)日：2007-01-04

申请号：US11261005

申请日：2005-10-28

申请人： Dana Bookbinder ,  Kenneth Hrdina ,  Glenn Kohnke ,  Lisa Moore ,  Susan Schiefelbein ,  Charlene Smith ,  Ulrich Neukirch

发明人： Dana Bookbinder ,  Kenneth Hrdina ,  Glenn Kohnke ,  Lisa Moore ,  Susan Schiefelbein ,  Charlene Smith ,  Ulrich Neukirch

IPC分类号： C03C3/06 ,  C03B32/00 ,  C03C23/00

CPC分类号： C03C3/06 ,  C03C4/0071 ,  C03C4/0085 ,  C03C2201/21 ,  C03C2201/23 ,  C03C2201/54

摘要： Disclosed in the application are a synthetic silica glass having low fluence-dependent transmission, particularly at about 193 nm, and a process for making the same. The glass may desirably exhibit a low level of fluorescence at 290 and 390 nm when activated at about 248 nm. The glass may desirably exhibit low level of LIWFD, [SiH*] and/or [ODC].

摘要翻译： 在本申请中公开了具有低注射度依赖性透射率，特别是约193nm的合成二氧化硅玻璃及其制造方法。 当在约248nm激活时，该玻璃可期望地在290和390nm处表现出低水平的荧光。 玻璃可能期望显示低水平的LIWFD，[SiH *]和/或[ODC]。

公开(公告)号：US20060137398A1

公开(公告)日：2006-06-29

申请号：US11148764

申请日：2005-06-08

申请人： Daniel Bleaking ,  Dana Bookbinder ,  Richard Fiacco ,  Kenneth Hrdina ,  Pushkar Tandon ,  John Maxon ,  Kimberly Wilbert

发明人： Daniel Bleaking ,  Dana Bookbinder ,  Richard Fiacco ,  Kenneth Hrdina ,  Pushkar Tandon ,  John Maxon ,  Kimberly Wilbert

IPC分类号： C03B20/00 ,  C03C3/06

CPC分类号： C03C3/06 ,  C03B19/1453 ,  C03B2201/03 ,  C03B2201/04 ,  C03B2201/07 ,  C03B2201/075 ,  C03B2201/21 ,  C03B2201/23 ,  C03C2201/12 ,  C03C2201/21 ,  C03C2201/23

摘要： Disclosed are high purity synthetic silica glass material having a high OH concentration homogeneity in a plane perpendicular to the optical axis, and process of making the same. The glass has high refractive index homogeneity. The glass can have high internal transmission of at least 99.65%/cm at 193 nm. The process does not require a post-sintering homogenization step. The controlling factors for high compositional homogeneity, thus high refractive index homogeneity, include high initial local soot density uniformity in the soot preform and slow sintering, notably isothermal treatment during consolidation.

公开(公告)号：US20060162382A1

公开(公告)日：2006-07-27

申请号：US11323948

申请日：2005-12-29

申请人： Kenneth Hrdina ,  Terry Taft ,  Michael Wasilewski

发明人： Kenneth Hrdina ,  Terry Taft ,  Michael Wasilewski

IPC分类号： C03B19/10

CPC分类号： C01B33/183 ,  C03B19/06 ,  C03B19/106 ,  C03B2201/02 ,  C03B2201/42 ,  C03B2207/32 ,  C03B2207/34

摘要： Disclosed are process and apparatus for making oxide soot particles where an atomizing burner is used as well as process for making densified silica-containing glass bodies by using soot particles having specific surface area of less than about 50 m2/g. Large glass bodies can be produced with less drying time and less binders by using such particles. The invention is particularly advantageous for the production of TiO2-doped silica glass.

摘要翻译： 公开了用于制造使用雾化燃烧器的氧化物烟灰颗粒的方法和装置，以及通过使用比表面积小于约50m 2的烟灰颗粒来制造致密的含二氧化硅的玻璃体的方法。 /G。 通过使用这样的颗粒，可以生产较少的干燥时间和较少粘合剂的大玻璃体。 本发明对于制备二氧化钛二氧化硅玻璃是特别有利的。

公开(公告)号：US5240493A

公开(公告)日：1993-08-31

申请号：US821228

申请日：1992-01-16

申请人： Yong S. Zhen ,  Kenneth Hrdina

发明人： Yong S. Zhen ,  Kenneth Hrdina

IPC分类号： B01J19/00 ,  B22F9/22 ,  B22F9/30 ,  C01B13/18 ,  C01F7/30 ,  C01G25/02 ,  C01G37/00 ,  C01G37/14 ,  C01G49/00 ,  C08J9/02 ,  C08L75/00 ,  C08L75/04

CPC分类号： B82Y30/00 ,  B22F9/22 ,  B22F9/30 ,  C01B13/18 ,  C01F7/308 ,  C01G25/02 ,  C01G37/006 ,  C01G37/14 ,  C01G49/0027 ,  C01P2004/52 ,  C01P2004/62 ,  C01P2004/64 ,  C01P2006/10 ,  C01P2006/12 ,  C01P2006/22 ,  H01M2300/0051

摘要： A process for preparing uniform, agglomerate free, submicron/nanosize ceramic powders from a polymeric foam comprising metal cations homogeneously incorporated within a foam cell structure of the polymeric foam. The polymeric foam is heated to remove any solvent, and calcined at a temperature of about 400.degree. C. to about 1200.degree. C. for about 1/2 to about 8 hours to produce the desired ceramic or metal powder.

公开(公告)号：US20060179879A1

公开(公告)日：2006-08-17

申请号：US11316293

申请日：2005-12-21

申请人： Adam Ellison ,  Kenneth Hrdina ,  Sabyasachi Sen

发明人： Adam Ellison ,  Kenneth Hrdina ,  Sabyasachi Sen

IPC分类号： C03B19/06 ,  C03B25/00

CPC分类号： C03C3/06 ,  C03B19/1415 ,  C03B19/143 ,  C03B19/1453 ,  C03B2201/12 ,  C03B2201/20 ,  C03B2201/23 ,  C03B2201/30 ,  C03B2201/31 ,  C03B2201/32 ,  C03B2201/34 ,  C03B2201/40 ,  C03B2201/42 ,  C03B2207/30 ,  C03B2207/32 ,  C03C4/0085 ,  C03C2201/42

摘要： The invention is directed to ultra-low expansion glasses to which adjustments have been made to selected variables in order to improve the properties of the glasses, and particularly to lower the expansivity of the glasses. The glasses are titania-doped silica glasses. The variables being adjusted include an adjustment in β-OH level; an adjustment to the cooling rate of the molten glass material through the setting point; and the addition of selected dopants to impact the CTE behavior.

摘要翻译： 本发明涉及对所选择的变量进行调整的超低膨胀玻璃，以改善玻璃的性能，特别是降低玻璃的膨胀性。 眼镜是二氧化钛掺杂的二氧化硅玻璃。 调整的变量包括β-OH水平的调整; 调整熔融玻璃材料通过凝固点的冷却速度; 并添加选定的掺杂剂以影响CTE行为。

公开(公告)号：US6093234A

公开(公告)日：2000-07-25

申请号：US246324

申请日：1994-05-19

申请人： Yong S. Zhen ,  Kenneth Hrdina

发明人： Yong S. Zhen ,  Kenneth Hrdina

IPC分类号： B01J19/00 ,  B01J23/75 ,  B01J37/00 ,  B22F9/16 ,  B22F9/22 ,  B22F9/30 ,  C01B13/18 ,  C01F7/30 ,  C01G3/00 ,  C01G9/02 ,  C01G25/00 ,  C01G25/02 ,  C01G37/00 ,  C01G37/14 ,  C01G45/00 ,  C01G49/00 ,  C01G49/02 ,  C01G51/04 ,  C01G53/04 ,  C04B38/00 ,  C08J9/02 ,  C08L75/00 ,  C08L75/04 ,  H01M4/86 ,  H01M4/90 ,  H01M8/02 ,  H01M8/12 ,  H01M8/14

CPC分类号： B82Y30/00 ,  B01J23/75 ,  B01J37/0018 ,  B22F9/22 ,  B22F9/30 ,  C01B13/18 ,  C01B13/185 ,  C01F7/308 ,  C01G25/00 ,  C01G25/02 ,  C01G3/006 ,  C01G37/006 ,  C01G37/14 ,  C01G45/1264 ,  C01G49/0027 ,  C01G49/02 ,  C01G51/04 ,  C01G53/04 ,  C01G9/02 ,  H01M4/8621 ,  H01M4/9016 ,  H01M4/9033 ,  H01M8/0215 ,  H01M8/1253 ,  B22F2998/00 ,  C01P2004/52 ,  C01P2004/62 ,  C01P2004/64 ,  C01P2006/10 ,  C01P2006/12 ,  C01P2006/22 ,  H01M2008/1293 ,  H01M2008/147 ,  H01M2300/0051 ,  H01M2300/0074 ,  H01M8/0219 ,  H01M8/126 ,  Y02E60/525 ,  Y02E60/526 ,  Y02P70/56

摘要： A process for preparing uniform, agglomerate free, submicron/nanosize ceramic powders from a polymeric foam comprising metal cations homogeneously incorporated within a foam cell structure of the polymeric foam. The polymeric foam is heated to remove any solvent, and calcined at a temperature of about 400.degree. C. to about 1400.degree. C. for about 1 minute to about 96 hours to produce the desired ceramic or metal powder.

摘要翻译： 一种由聚合物泡沫制备均匀的无聚集的亚微米/纳米尺寸陶瓷粉末的方法，其包括均匀地结合在聚合物泡沫的泡沫单元结构内的金属阳离子。 加热聚合物泡沫以除去任何溶剂，并在约400℃至约1400℃的温度下煅烧约1分钟至约96小时以产生所需的陶瓷或金属粉末。

公开(公告)号：US5338334A

公开(公告)日：1994-08-16

申请号：US49081

申请日：1993-04-20

申请人： Yong S. Zhen ,  Kenneth Hrdina

发明人： Yong S. Zhen ,  Kenneth Hrdina

IPC分类号： B01J19/00 ,  B01J23/75 ,  B01J37/00 ,  B22F9/16 ,  B22F9/22 ,  B22F9/30 ,  C01B13/18 ,  C01F7/30 ,  C01G3/00 ,  C01G9/02 ,  C01G25/00 ,  C01G25/02 ,  C01G37/00 ,  C01G37/14 ,  C01G45/00 ,  C01G49/00 ,  C01G49/02 ,  C01G51/04 ,  C01G53/04 ,  C04B38/00 ,  C08J9/02 ,  C08L75/00 ,  C08L75/04 ,  H01M4/86 ,  H01M4/90 ,  H01M8/02 ,  H01M8/12 ,  H01M8/14 ,  C04B38/02

CPC分类号： B82Y30/00 ,  B01J23/75 ,  B01J37/0018 ,  B22F9/22 ,  B22F9/30 ,  C01B13/18 ,  C01B13/185 ,  C01F7/308 ,  C01G25/00 ,  C01G25/02 ,  C01G3/006 ,  C01G37/006 ,  C01G37/14 ,  C01G45/1264 ,  C01G49/0027 ,  C01G49/02 ,  C01G51/04 ,  C01G53/04 ,  C01G9/02 ,  H01M4/8621 ,  H01M4/9016 ,  H01M4/9033 ,  H01M8/0215 ,  H01M8/1253 ,  B22F2998/00 ,  C01P2004/52 ,  C01P2004/62 ,  C01P2004/64 ,  C01P2006/10 ,  C01P2006/12 ,  C01P2006/22 ,  H01M2008/1293 ,  H01M2008/147 ,  H01M2300/0051 ,  H01M2300/0074 ,  H01M8/0219 ,  H01M8/126 ,  Y02E60/525 ,  Y02E60/526 ,  Y02P70/56

摘要： A for preparing uniform, agglomerate free, submicron/nanosize ceramic powders from a polymeric foam comprising metal cations homogeneously incorporated within a foam cell structure of the polymeric foam. The polymeric foam is heated to remove any solvent, and calcined at a temperature of about 400.degree. C. to about 1400.degree. C. for about 1 minute to about 96 hours to produce the desired ceramic or metal powder.

摘要翻译： A，用于从聚合物泡沫制备均匀的无团聚，亚微米/纳米尺寸的陶瓷粉末，其包括均匀地结合在聚合物泡沫的泡沫单元结构内的金属阳离子。 加热聚合物泡沫以除去任何溶剂，并在约400℃至约1400℃的温度下煅烧约1分钟至约96小时以产生所需的陶瓷或金属粉末。

公开(公告)号：US20070042892A1

公开(公告)日：2007-02-22

申请号：US11589584

申请日：2006-10-30

申请人： Steven Dawes ,  Richard Fiacco ,  Kenneth Hrdina ,  Michael Wasilewski

发明人： Steven Dawes ,  Richard Fiacco ,  Kenneth Hrdina ,  Michael Wasilewski

IPC分类号： C03C3/06

CPC分类号： C03B19/06 ,  C03B19/02 ,  C03B19/12 ,  C03B2201/42 ,  C03C3/06 ,  C03C2201/42 ,  C03C2203/20

摘要： The present invention provides doped titania-doped silica glass articles having low thermal expansions and low variations in thermal expansion. According to one embodiment of the invention, a titania-doped silica glass article has a titania content of between about 5 wt % and about 9 wt %; a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C.; and a variation in coefficient of thermal expansion of less than about 5 ppb/° C. at a temperature between 15° C and 30° C.