摘要:
In a process for manufacturing an interior fitted part for motor vehicles, such as an inside roof lining for automobiles, a staple-fiber formed fabric of a drawn polyethylene terephthalate matrix component and of a binding component is subjected at least once during the process to an annealing process, which increases the thermal stability of the fitted part. Also disclosed is a fitted part manufactured by this method.
摘要:
A hook and loop fastener for flat structures, particularly for textile products, having a hook part and an interlocking part, the interlocking part being made of a nonwoven composite having worked-in, textured, polymeric threads, the nonwoven composite being used as support for the textured threads, and the textured threads forming the loops for the hooks.
摘要:
The invention relates to a textile fabric having a coating composed of two layers of thermoplastic hot-seal adhesives of differing compositions applied one on top of the other, the second hot-seal adhesive, which is applied to the first, having a melting point of >135° C. and a melt flow index (MFI) value of 50 to 250 g/10 minutes (190° C./2.16 kg). The invention further relates to a method for producing a textile fabric, comprising the following steps: a) producing a textile fabric using a textile fabric manufacturing technique; b) applying a layer of a first hot-seal adhesive to the textile fabric; and c) applying a layer of a second hot-seal adhesive to the textile fabric so as to d) form a layer of the second hot-seal adhesive over the layer of first hot-seal adhesive, the second hot-seal adhesive used having a melting point of >135° C. and a melt flow index (MFI) value of 50 to 250 g/10 minutes (190° C./2.16 kg). The textile fabrics may be used as interlining or lining material which can withstand stress during care treatment.
摘要:
The invention relates to a textile fabric having a coating composed of two layers of thermoplastic hot-seal adhesives of differing compositions applied one on top of the other, the second hot-seal adhesive, which is applied to the first, having a melting point of >135° C. and a melt flow index (MFI) value of 50 to 250 g/10 minutes (190° C./2.16 kg). The invention further relates to a method for producing a textile fabric, comprising the following steps: a) producing a textile fabric using a textile fabric manufacturing technique; b) applying a layer of a first hot-seal adhesive to the textile fabric; and c) applying a layer of a second hot-seal adhesive to the textile fabric so as to d) form a layer of the second hot-seal adhesive over the layer of first hot-seal adhesive, the second hot-seal adhesive used having a melting point of >135° C. and a melt flow index (MFI) value of 50 to 250 g/10 minutes (190° C./2.16 kg). The textile fabrics may (be used as interlining or lining material which can withstand stress during care treatment.
摘要:
A laminate is claimed, having a first cover layer, a fabric with perforations as the middle layer, and a second cover layer, as are a method for its production and the use of the laminate as a fluid absorption and distribution layer made of a nonwoven fabric layer oriented in the Z direction, for absorbent hygiene articles. A three-dimensional form is achieved in that the fabric is present in the shrunk state in the middle layer, i.e. is brought into this state.
摘要:
Bodies containing superabsorber polymers, having superabsorber polymers bonded together with polymer fibers, wherein at least part of the superabsorber polymers are present as a microporous open-celled foam. The bodies are used for producing diapers, sanitary napkins, tampons and other articles of personal hygiene.
摘要:
A microporous, polymeric film is prepared by dissolving methylene-chloride-soluble, film-forming polymers completely in methylene chloride. Then an aqueous phase is prepared containing non-methylene-chloride-soluble, water-soluble thickeners and, if desired, additives, and brought to a viscosity of about 0.07 to 0.5 Pa s. The aqueous phase is then dispersed in the polymer solution and the resultant paste is spread onto a support material or intermediate support, the methylene chloride is evaporated, the resultant membrane is transferred to the actual support, and finally the water is removed by drying.
摘要:
Disclosed is a process for producing a surgical sponge which contains contrast agent embedded in a polymer matrix in proportions of up to 70 wt. %. The matrix consists of a polymer material free of plasticizers. In the process for the production of the sponge a matrix for the contrast agent is used, which is an uncrosslinked, viscous liquid, prepolymer state until after it has been extruded onto the basic fleece material, and not until a process step that then follows is the polymerization completed.
摘要:
A three-dimensionally structured fibrous web made up of continuous-filament layers which alternate perpendicular to the surface plane, and denser short-fiber layers that are permanently thermally bonded in a continuous or spot-like manner to the filament layers, the wide-mesh continuous-filament layers representing a scrim, lattice, or netting, has on the short-fiber layers repeating, fold- or wave-shaped elevations. In the manufacturing process, all of the layers of the laminate are subjected together to a shrinkage process at a temperature which lies between the softening and melting points of the scrim material.
摘要:
The invention disclosed herein relates to a method for bonding the opposing surfaces of textile materials to each other with a heat-seal adhesive. The heat-seal adhesive is a polyurethane urea heat-seal adhesive prepared by first preparing a chain-extended polyurethane from at least one diisocyanate, at least one polydiol, and chain-extenders. The chain-extenders may comprise a mixture of low molecular weight diols comprised of at least one low molecular weight diol having a molecular weight below about 500 and having side chains or ether groups, and at least one unbranched low molecular weight diol having a molecular weight below about 500. The chain-extended polyurethane has a free-isocyanate group content which comprises from about 10 to about 40 mole percent of the isocyanate content of the starting mixture. An emulsifier is added to the chain-extended polyurethane, and the polyurethane and emulsifier mixture is emulsified with water. Diamines or diamine mixtures may be added to the emulsion.