摘要:
Disclosed is a thin plate member for forming a semiconductor package, having a recess for receiving a semiconductor chip. The thin plate is composed of sintered metal, e.g. sintered copper or sintered alluminum alloy. A sintered metal body being porous and having a shape which is close to the shape of the thin plate member is prepared, and it is sized into the shape of the thin plate member. The sintered alluminum alloy comprises 0.4 to 0.8% by weight of magnesium, 0.2 to 0.6% by weight of silicon and the balance aluminum and has a structure comprising an aluminum phase being formed of aluminum particles and an alloy phase being composed of magnesium, silicon and aluminum and interposing between the aluminum particles, and the sintered copper has a metallographic structure comprising a phase of copper particles.
摘要:
In a method of manufacturing a sheet member comprising: obtaining a sintered compact by sintering a sheet-like compact having a reduced-thickness portion and an enlarged-thickness portion; and then repressing the sintered compact into a sheet member, a difference in density between the reduced-thickness portion and the enlarged-thickness portion of the sintered compact after repressing is adjusted to be in a range of .+-.1.5%. By doing so, the accuracy of flatness is enhanced and the amount of distortion, which would otherwise remain in the sheet member, is reduced because the sheet member is formed by sintering the sheet-like compact. In addition, the deformation caused by heating is greatly restricted. Accordingly, the prospect of the sheet member of the present invention is bright as a heat dissipating plate.
摘要:
There is provided a connecting rod including a connecting rod body and a cap having excellent alignment properties, and a method of producing such a connecting rod. A connecting rod body and a cap are produced through the steps of molding green compacts respectively corresponding to the connecting rod body and the cap; sintering and unifying both the green compacts; forging the resultant sintered product in a mold; and fracturing the resultant forged product. The green compact corresponding to the cap and/or the green compact corresponding to the connecting rod body includes opposite circumferential end faces formed with one or more projection. A clearance c is formed between both circumferential end faces of the sintered product due to the projection. With this clearance c, both the circumferential end faces are formed with recesses and projections which are fitted to each other during the forging process and which are relatively large and thus have large biting amounts. During the fracturing process, the recesses and the projections are separated into two pieces.
摘要:
A plurality of blanks divided at a division end face 5 or a blank-bonded product comprising a plurality of blanks sintered and bonded together are or is compressed in the same mold, so that they are plastically deformed until the division end faces 5 are cohered. Thereafter, a load is applied to the plastically worked product in a direction of breaking of the division end faces 5 to break the division end faces 5 and divide the plastically worked product into a plurality of members. In this manner, a split type mechanical part having irregularities meshed with each other on mating faces and easily positionable relative to each other can be produced with a good dimentional accuracy.
摘要:
The Al-Si sintered alloy having good mechanical strength and elongation and is especially excellent in wear resistance, and a method for producing the same. The sintered alloy consists of 2.4-23.5% Si, 2-5% Cu, 0.2-1.5% Mg, 0.01-1% of transition metals and the balance of aluminum and unavoidable impurities, and has a dapple grain structure of an Al-solid solution phase and an Al-Si alloy phase containing dispersed pro-eutectic Si crystals having a maximum diameter of 5-60 .mu.m either in the whole body or in the surface contact portion, and the area ratio of the Al-solid solution phase in the grain structure is in the range of 20-80%.
摘要:
There is disclosed a method for manufacturing an Fe-based sintered alloy which is superb in machinability. This process comprises the steps of coating a paste-like coating agent including a compound of boron to a surface of a compact of Fe-based or Fe, Cu-based sintered alloy powder including carbon or a pre-sintered compact obtained by heating the compact at a diffusion temperature or less of carbon, and sintering a resultant compact or a pre-sintered compact at a diffusion temperature or more of carbon. An Fe-based sintered alloy manufactured through this process and a bearing cap made of such an Fe-based sintered alloy are also disclosed. In the invention, a film including a compound of boron and pyrolytic resin can be used instead of the paste-like coating agent.
摘要:
A method of manufacturing sintered Al-Si series alloy parts having complex configurations such as scroll shaped parts wherein Al-Si series alloy powder solidified via rapid cooling prepared by adding effective components such as Si, Cu, Mg, Fe, Mn, Zr and Ce to Al is compression molded, the molded body is sintered by heating via an electrical current conduction in a form of a plasma discharge and then the sintered body is worked by pressing, thereby the parts having complex configurations of light weight, high mechanical strength and toughness is manufactured with a simple installation and reduced processing manhours, and with a high efficiency and at a low cost.
摘要:
A fluid dynamic pressure bearing composed of a cylindrical sintered compact includes: a thrust region which is formed on an end surface of the bearing and receives at least a thrust load; a roughed portion having small peaks and valleys formed on the thrust region; and thrust recesses for generating thrust fluid dynamic pressure, which are formed on the thrust region.
摘要:
The present invention relates to a method for producing, without quench-hardening process, a ferrous sintered alloy having satisfactory strength which is equal to that of the conventional ferrous sintered quenched material, and the method comprises the steps of: preparing a powder mixture by adding, in weight ratios, 1 to 2% of copper powder, 1 to 3% of Ni powder, and graphite to a ferrous alloy powder consisting of 3 to 5% of Ni, 0.4 to 0.7% of Mo, and the remainder Fe, the quantity of said graphite being determined such that the C-content after sintering is 0.2 to 0.7%; compacting said powder mixture in a tool to form a green compact; sintering said green compact in a non-oxidizing atmosphere at a temperature in the range of 1130.degree. to 1230.degree. C.; and cooling the sintered product in the sintering furnace at a rate of 5.degree. C./min. to 20.degree. C./min.
摘要:
A fluid dynamic pressure effect can be sufficient without receiving a large effect of viscous friction of lubricating oil with changes in the environmental temperature in which it is used, and smooth starting of the rotating shaft can be ensured by regulating the gap between the rotating shaft and bearing within a suitable range. An outer diameter of the bearing, D, a length in an axial direction of the bearing, L, a gap at a radial side which is between the rotating shaft and the bearing, C, and an inclining height of the bearing end surface to which the flange is faced, δ, satisfy the expression L/D
摘要翻译:流体动力学效应可以充分发挥润滑油在使用环境温度变化的作用下的粘性摩擦力的大的影响,通过调整旋转轴与旋转轴之间的间隙可以确保旋转轴的平滑启动 在适当的范围内。 轴承的外径D,轴承的轴向长度L,在旋转轴与轴承之间的径向侧的间隙C和轴承端面的倾斜高度,其中 法兰面对,δ,满足表达式L / D