公开(公告)号：US20130048905A1

公开(公告)日：2013-02-28

申请号：US13583115

申请日：2011-03-04

申请人： Tetsuro Tohma ,  Kentaro Iwasaki

发明人： Tetsuro Tohma ,  Kentaro Iwasaki

IPC分类号： C09K3/00 ,  C04B35/64

CPC分类号： C04B38/0645 ,  C04B35/478 ,  C04B35/63488 ,  C04B2111/00793 ,  C04B2235/3206 ,  C04B2235/3217 ,  C04B2235/3218 ,  C04B2235/322 ,  C04B2235/3232 ,  C04B2235/3418 ,  C04B2235/36 ,  C04B2235/3852 ,  C04B2235/3886 ,  C04B2235/401 ,  C04B2235/402 ,  C04B2235/404 ,  C04B2235/428 ,  C04B2235/44 ,  C04B2235/441 ,  C04B2235/442 ,  C04B2235/443 ,  C04B2235/444 ,  C04B2235/446 ,  C04B2235/447 ,  C04B2235/448 ,  C04B2235/449 ,  C04B2235/5436 ,  C04B2235/5445 ,  C04B2235/5463 ,  C04B2235/6584 ,  C04B2235/661 ,  C04B2235/79 ,  C04B38/0006 ,  C04B38/0074

摘要： The production method of the present invention is a method for producing porous aluminum magnesium titanate by forming a mixture containing Al source powder, Mg source powder, Ti source powder and Si source powder as well as a pore-forming agent to obtain a molded body; presintering the obtained molded body; and then sintering the presintered molded body, wherein the content of the pore-forming agent to a total of 100 parts by mass for the Al source powder, Mg source powder, Ti source powder and Si source powder is 5 to 30 parts by mass, the melting point of the Si source powder is 600 to 1300° C., when the elemental composition ratio of Al, Mg, Ti and Si in the mixture is represented by compositional formula (1): Al2(1−x)MgxTi(1+x)O5+aAl2O3+bSiO2   (1), x satisfies 0.05≦x≦0.15, a satisfies 0≦a≦0.1 and b satisfies 0.05≦b≦0.15, and the presintered molded body is sintered at 1300 to 1560° C.

摘要翻译： 本发明的制造方法是通过形成含有Al源粉末，Mg源粉末，Ti源粉末和Si源粉末以及成孔剂的混合物来制造多孔钛酸镁铝的方法，以获得成型体; 预先烧结所得成型体; 然后烧结预烧结成形体，其中对于Al源粉末，Mg源粉末，Ti源粉末和Si源粉末，造孔剂的含量总共为100质量份，为5〜30质量份， 当混合物中Al，Mg，Ti和Si的元素组成比由组成式（1）表示时，Si源粉末的熔点为600〜1300℃：Al 2（1-x）Mg x Ti + x）O5 + aAl2O3 + bSiO2（1），x满足0.05＆nlE; x＆nlE; 0.15，a满足0＆nlE; a＆nlE; 0.1和b满足0.05＆nlE; b＆nlE; 0.15，预烧结成型体在1300〜 C。

公开(公告)号：US20120311985A1

公开(公告)日：2012-12-13

申请号：US13519244

申请日：2010-12-24

申请人： Kentaro Iwasaki ,  Tetsuro Tohma

发明人： Kentaro Iwasaki ,  Tetsuro Tohma

IPC分类号： C04B35/478 ,  B01D39/20 ,  C04B35/46

CPC分类号： C04B35/478 ,  C01G23/002 ,  C01G23/003 ,  C04B38/0006 ,  C04B2111/00793 ,  C04B2235/3206 ,  C04B2235/3217 ,  C04B2235/3218 ,  C04B2235/3222 ,  C04B2235/3232 ,  C04B2235/3237 ,  C04B2235/3281 ,  C04B2235/3418 ,  C04B2235/3427 ,  C04B2235/3463 ,  C04B2235/36 ,  C04B2235/3826 ,  C04B2235/3852 ,  C04B2235/3873 ,  C04B2235/3886 ,  C04B2235/401 ,  C04B2235/402 ,  C04B2235/404 ,  C04B2235/407 ,  C04B2235/44 ,  C04B2235/441 ,  C04B2235/446 ,  C04B2235/5436 ,  C04B2235/5445 ,  C04B2235/5481 ,  C04B2235/652 ,  C04B2235/658 ,  C04B2235/81 ,  C04B2235/9607 ,  F01N3/0222

摘要： The present invention is a process for producing an aluminum titanate-based ceramics comprising a step of firing a starting material mixture containing a titanium source powder, an aluminum source powder, and a copper source.

摘要翻译： 本发明是一种钛酸铝系陶瓷的制造方法，其特征在于，包括对含有钛源粉末，铝源粉末和铜源的原料混合物进行烧成的工序。

公开(公告)号：US08921249B2

公开(公告)日：2014-12-30

申请号：US13583115

申请日：2011-03-04

申请人： Tetsuro Tohma ,  Kentaro Iwasaki

发明人： Tetsuro Tohma ,  Kentaro Iwasaki

IPC分类号： C04B35/00 ,  C04B38/06 ,  C04B35/478 ,  C04B35/634 ,  C04B111/00

CPC分类号： C04B38/0645 ,  C04B35/478 ,  C04B35/63488 ,  C04B2111/00793 ,  C04B2235/3206 ,  C04B2235/3217 ,  C04B2235/3218 ,  C04B2235/322 ,  C04B2235/3232 ,  C04B2235/3418 ,  C04B2235/36 ,  C04B2235/3852 ,  C04B2235/3886 ,  C04B2235/401 ,  C04B2235/402 ,  C04B2235/404 ,  C04B2235/428 ,  C04B2235/44 ,  C04B2235/441 ,  C04B2235/442 ,  C04B2235/443 ,  C04B2235/444 ,  C04B2235/446 ,  C04B2235/447 ,  C04B2235/448 ,  C04B2235/449 ,  C04B2235/5436 ,  C04B2235/5445 ,  C04B2235/5463 ,  C04B2235/6584 ,  C04B2235/661 ,  C04B2235/79 ,  C04B38/0006 ,  C04B38/0074

摘要： The production method of the present invention is a method for producing porous aluminum magnesium titanate by forming a mixture containing Al source powder, Mg source powder, Ti source powder and Si source powder as well as a pore-forming agent to obtain a molded body; presintering the obtained molded body; and then sintering the presintered molded body, wherein the content of the pore-forming agent to a total of 100 parts by mass for the Al source powder, Mg source powder, Ti source powder and Si source powder is 5 to 30 parts by mass, the melting point of the Si source powder is 600 to 1300° C., when the elemental composition ratio of Al, Mg, Ti and Si in the mixture is represented by compositional formula (1): Al2(1−x)MgxTi(1+x)O5+aAl2O3+bSiO2   (1), x satisfies 0.05≦x≦0.15, a satisfies 0≦a≦0.1 and b satisfies 0.05≦b≦0.15, and the presintered molded body is sintered at 1300 to 1560° C.

摘要翻译： 本发明的制造方法是通过形成含有Al源粉末，Mg源粉末，Ti源粉末和Si源粉末以及成孔剂的混合物来制造多孔钛酸镁铝的方法，以获得成型体; 预先烧结所得成型体; 然后烧结预烧结成形体，其中对于Al源粉末，Mg源粉末，Ti源粉末和Si源粉末，造孔剂的含量总共为100质量份，为5〜30质量份， 当混合物中Al，Mg，Ti和Si的元素组成比由组成式（1）表示时，Si源粉末的熔点为600〜1300℃：Al 2（1-x）Mg x Ti + x）O5 + aAl2O3 + bSiO2（1），x满足0.05＆nlE; x＆nlE; 0.15，a满足0＆nlE; a＆nlE; 0.1和b满足0.05＆nlE; b＆nlE; 0.15，预烧结成型体在1300〜 C。

公开(公告)号：US20140065350A1

公开(公告)日：2014-03-06

申请号：US14008358

申请日：2012-03-09

申请人： Yasuharu Kobashi ,  Tetsuro Tohma ,  Kentaro Iwasaki

发明人： Yasuharu Kobashi ,  Tetsuro Tohma ,  Kentaro Iwasaki

IPC分类号： C04B38/00

CPC分类号： B01D46/2429 ,  B01D46/2425 ,  B01D2046/2496 ,  C04B35/465 ,  C04B35/478 ,  C04B38/0009 ,  C04B2111/00793 ,  C04B2111/0081 ,  C04B2235/3206 ,  C04B2235/3217 ,  C04B2235/3232 ,  C04B2235/3418 ,  C04B2235/3463 ,  C04B2235/5436 ,  C04B2235/5445 ,  C04B2235/6021 ,  C04B2235/80 ,  Y10T428/24149 ,  C04B38/0012 ,  C04B38/0054 ,  C04B38/0074 ,  C04B38/0645

摘要： A honeycomb structure 100 has a plurality of flow paths 110a and 110b which are partitioned by partition walls 120 and are substantially parallel to each other; and one end of the flow path 110a is plugged by a plugging part 130 at one end surface 100a of the honeycomb structure 100, and one end of the flow path 110b is plugged by a plugging part 130 at the other end surface 100b of the honeycomb structure 100, wherein, in an image of the partition walls 120 obtained by X-ray CT measurement, when the number of communicating holes detected when resolution of the image is 1.5 μm/pixel is defined as X, and the number of communicating holes detected when resolution of the image is 2.5 μam/pixel is defined as Y, Y/X is 0.58 or more.

摘要翻译： 蜂窝结构体100具有由分隔壁120隔开并且基本上彼此平行的多个流路110a和110b; 流路110a的一端由蜂窝结构体100的一个端面100a处的堵塞部130堵塞，流路路径110b的一端在蜂窝体的另一端面100b处被堵塞部130堵塞 结构100，其中，在通过X射线CT测量获得的分隔壁120的图像中，当图像的分辨率为1.5μm/像素时检测到的连通孔的数量被定义为X，并且检测到连通孔的数量 当图像的分辨率为2.5μm/像素时，Y / X为0.58以上。

公开(公告)号：US20120275986A1

公开(公告)日：2012-11-01

申请号：US13499174

申请日：2010-09-28

申请人： Kentaro Iwasaki ,  Akiyoshi Nemoto ,  Tetsuro Tohma

发明人： Kentaro Iwasaki ,  Akiyoshi Nemoto ,  Tetsuro Tohma

IPC分类号： C03C8/02 ,  C01B31/00

CPC分类号： B01J23/04 ,  B01D53/944 ,  B01D2255/2022 ,  B01D2255/2027 ,  B01D2255/2045 ,  B01D2255/30 ,  B01D2255/9202 ,  B01J21/08 ,  C03C8/02

摘要： The present invention is a glass frit comprising 60 to 80% by weight of SiO2, 9 to 20% by weight of Al2O3, 3 to 12% by weight of K2O, and 3 to 12% by weight of Na2O, expressed on oxide basis.

摘要翻译： 本发明是以氧化物为基准，含有60〜80重量％的SiO 2，9〜20重量％的Al 2 O 3，3〜12重量％的K 2 O，3〜12重量％的Na 2 O。

公开(公告)号：US20130062275A1

公开(公告)日：2013-03-14

申请号：US13635561

申请日：2011-03-16

申请人： Yasuharu Kobashi ,  Tetsuro Tohma ,  Kentaro Iwasaki

发明人： Yasuharu Kobashi ,  Tetsuro Tohma ,  Kentaro Iwasaki

IPC分类号： B29C67/20 ,  B01D24/00 ,  B01D39/14

CPC分类号： B01D46/0001 ,  B01D24/001 ,  B01D39/14 ,  B01D39/2093 ,  B01D46/2429 ,  B01D46/2474 ,  B01D2239/10 ,  B01J35/04 ,  B29C67/202 ,  C04B35/478 ,  C04B35/638 ,  C04B38/0006 ,  C04B38/0009 ,  C04B2111/00793 ,  C04B2111/0081 ,  C04B2235/3206 ,  C04B2235/3218 ,  C04B2235/3222 ,  C04B2235/3234 ,  C04B2235/3418 ,  C04B2235/3427 ,  C04B2235/3463 ,  C04B2235/36 ,  C04B2235/3826 ,  C04B2235/3852 ,  C04B2235/3873 ,  C04B2235/3886 ,  C04B2235/401 ,  C04B2235/402 ,  C04B2235/441 ,  C04B2235/446 ,  C04B2235/449 ,  C04B2235/5436 ,  C04B2235/5472 ,  C04B2235/652 ,  C04B2235/658 ,  C04B2235/6584 ,  C04B2235/80 ,  F01N3/0222 ,  C04B38/0054 ,  C04B38/0074

摘要： A method of manufacturing a honeycomb structure comprises a step of forming a molded article by molding a raw material containing a ceramic powder and a pore-forming agent; and a step of manufacturing a honeycomb structure by sintering the molded article, wherein the pore-forming agent is powder formed of a material that disappears at a sintering temperature or less where the molded article is sintered, the powder is obtained by mixing a small particle size powder and a large particle size powder, a median particle size of which a ratio of a cumulative mass with respect to a total mass of the small particle size powder is 50% is 5 to 20 μm, a median particle size of which a ratio of a cumulative mass with respect to a total mass of the large particle size powder is 50% is 30 μm or more, and a ninety-percentage particle size of which a ratio of a cumulative mass with respect to a total mass of the large particle size powder is 90% is 80 μm or less.

摘要翻译： 一种蜂窝结构体的制造方法，其特征在于，包括通过成型含有陶瓷粉末和成孔剂的原料形成成形品的工序; 以及通过烧结成型制品来制造蜂窝结构体的步骤，其中成孔剂是在烧结温度以下烧成的材料消失的粉末形成的粉末，粉末是将小粒子 粒径粉末和大粒径粉末，其中累积质量相对于小粒径粉末的总质量的比例为50％的中值粒径为5〜20μm，其中比粒径 相对于大粒径粉末的总质量为50％的累积质量为30μm以上，相对于大粒子的总质量的累积质量比为90％的粒径 尺寸为90％的粉末为80μm以下。

公开(公告)号：US20120198805A1

公开(公告)日：2012-08-09

申请号：US13389375

申请日：2010-08-10

申请人： Kentaro Iwasaki ,  Tetsuro Tohma ,  Kousuke Uoe

发明人： Kentaro Iwasaki ,  Tetsuro Tohma ,  Kousuke Uoe

IPC分类号： B01D39/20 ,  C04B35/478 ,  B32B3/12 ,  C04B35/64

CPC分类号： C04B35/478 ,  C04B2235/3206 ,  C04B2235/3251 ,  C04B2235/96 ,  Y10T428/24149

摘要： The present invention is a process for producing an aluminum titanate ceramics, comprising firing a starting material mixture containing a titanium source powder and an aluminum source powder, wherein a content of niobium, expressed on the oxide basis, is not less than 0.2 parts by mass and not more than 2.5 parts by mass in 100 parts by mass of the starting material mixture.

摘要翻译： 本发明是一种制造钛酸铝陶瓷的方法，包括焙烧含有钛源粉末和铝源粉末的原料混合物，其中以氧化物为基准的铌含量不小于0.2质量份 在100质量份原料混合物中不超过2.5质量份。

公开(公告)号：US20110248106A1

公开(公告)日：2011-10-13

申请号：US13124079

申请日：2009-11-05

申请人： Hajime Maki ,  Kousuke Uoe ,  Kentaro Iwasaki

发明人： Hajime Maki ,  Kousuke Uoe ,  Kentaro Iwasaki

IPC分类号： B02C23/00 ,  C04B35/478 ,  C03C14/00 ,  C04B35/622

CPC分类号： C04B35/478 ,  C04B35/6261 ,  C04B35/6262 ,  C04B2235/3206 ,  C04B2235/3222 ,  C04B2235/3418 ,  C04B2235/3427 ,  C04B2235/3463 ,  C04B2235/36 ,  C04B2235/3826 ,  C04B2235/3852 ,  C04B2235/3873 ,  C04B2235/3886 ,  C04B2235/401 ,  C04B2235/402 ,  C04B2235/404 ,  C04B2235/44 ,  C04B2235/441 ,  C04B2235/442 ,  C04B2235/444 ,  C04B2235/446 ,  C04B2235/447 ,  C04B2235/448 ,  C04B2235/449 ,  C04B2235/5409 ,  C04B2235/5436 ,  C04B2235/5445 ,  C04B2235/5481 ,  C04B2235/656 ,  C04B2235/81 ,  C04B2235/9607

摘要： The invention is to provide a novel process for producing aluminum titanate-based ceramics having a low coefficient of thermal expansion. The invention is a process for producing an aluminum titanate-based ceramic comprising firing a starting material mixture containing a titanium source powder, an aluminum source powder and a silicon source powder, wherein the particle diameter corresponding to a cumulative percentage of 50% (D50) on a volume basis of the silicon source powder is not greater than 5 μm. The invention includes the process wherein the starting material mixture further contains a magnesium source powder.

摘要翻译： 本发明提供一种制造热膨胀系数低的钛酸铝系陶瓷的新方法。 本发明是一种钛酸铝系陶瓷的制造方法，其特征在于，烧成含有钛源粉末，铝源粉末，硅源粉末的原料混合物，其中，相当于累积率为50％（D50）的粒径， 硅源粉末的体积基准不大于5μm。 本发明包括其中原料混合物还含有镁源粉末的方法。

公开(公告)号：US07381465B2

公开(公告)日：2008-06-03

申请号：US10505542

申请日：2003-02-17

申请人： Tsukasa Torimoto ,  Bunsho Ohtani ,  Kentaro Iwasaki

发明人： Tsukasa Torimoto ,  Bunsho Ohtani ,  Kentaro Iwasaki

IPC分类号： B32B5/16 ,  B05D7/00

CPC分类号： C01B19/007 ,  B01J13/02 ,  B01J13/025 ,  B01J27/04 ,  B01J31/0272 ,  B01J33/00 ,  B01J35/0013 ,  B01J35/004 ,  B82Y30/00 ,  C01G11/02 ,  C01P2004/03 ,  C01P2004/04 ,  C01P2004/34 ,  C01P2004/64 ,  C01P2004/82 ,  C09C3/12 ,  Y10S977/775 ,  Y10S977/777 ,  Y10S977/824 ,  Y10T428/2991

摘要： A core-shell structure comprises a core (2) comprising nanoparticles and a shell (4) coating the core (2), and its void space (3) formed by the core (2) and the shell (4) is controlled. A method of preparing the core-shell structure comprises: forming particles comprising a photoetchable semiconductor, metal or polymer and coating the particles with a shell (4) comprising a non-photoetchable semiconductor, metal or polymer, to form a core-shell structure (5); and irradiating the core-shell structure with a light having a controlled wavelength in the photoetching solution to form an adjustable void space inside a shell (3) within the core-shell structure by the size-selective photoetching method. The core-shell structure allows the preparation of a catalyst exhibiting an extremely high efficiency, and can be used as a precursor for preparing a nanomaterial required for a nanodevice.

摘要翻译： 芯壳结构包括包含纳米颗粒的芯（2）和涂覆芯（2）的壳（4），并且控制由芯（2）和壳（4）形成的空隙（3）。 制备核 - 壳结构的方法包括：形成包含可光取代半导体，金属或聚合物的颗粒并用包含不可光取代的半导体，金属或聚合物的壳（4）涂覆颗粒以形成核 - 壳结构（ 5）; 并且在光刻溶液中用具有受控波长的光照射核 - 壳结构，以通过尺寸选择性光刻法在芯 - 壳结构内的壳体（3）内部形成可调节的空隙空间。 核 - 壳结构允许制备显示出非常高效率的催化剂，并且可以用作制备纳米器件所需的纳米材料的前体。

公开(公告)号：US20050082521A1

公开(公告)日：2005-04-21

申请号：US10505542

申请日：2003-02-17

申请人： Tsukasa Torimoto ,  Bunsho Ohtani ,  Kentaro Iwasaki

发明人： Tsukasa Torimoto ,  Bunsho Ohtani ,  Kentaro Iwasaki

IPC分类号： B82B1/00 ,  B01J13/02 ,  B01J27/04 ,  B01J31/02 ,  B01J33/00 ,  B01J35/00 ,  B82B3/00 ,  C01G11/02 ,  H01L29/06

CPC分类号： C01B19/007 ,  B01J13/02 ,  B01J13/025 ,  B01J27/04 ,  B01J31/0272 ,  B01J33/00 ,  B01J35/0013 ,  B01J35/004 ,  B82Y30/00 ,  C01G11/02 ,  C01P2004/03 ,  C01P2004/04 ,  C01P2004/34 ,  C01P2004/64 ,  C01P2004/82 ,  C09C3/12 ,  Y10S977/775 ,  Y10S977/777 ,  Y10S977/824 ,  Y10T428/2991

摘要： A core-shell structure comprises a core (2) comprising nanoparticles and a shell (4) coating the core (2), and its void space (3) formed by the core (2) and the shell (4) is controlled. A method of preparing the core-shell structure comprises: forming particles comprising a photoetchable semiconductor, metal or polymer and coating the particles with a shell (4) comprising a non-photoetchable semiconductor, metal or polymer, to form a core-shell structure (5); and irradiating the core-shell structure with a light having a controlled wavelength in the photoetching solution to form an adjustable void space inside a shell (3) within the core-shell structure by the size-selective photoetching method. The core-shell structure allows the preparation of a catalyst exhibiting an extremely high efficiency, and can be used as a precursor for preparing a nanomaterial required for a nanodevice.

摘要翻译： 芯壳结构包括包含纳米颗粒的芯（2）和涂覆芯（2）的壳（4），并且控制由芯（2）和壳（4）形成的空隙（3）。 制备核 - 壳结构的方法包括：形成包含可光取代半导体，金属或聚合物的颗粒并用包含不可光取代的半导体，金属或聚合物的壳（4）涂覆颗粒以形成核 - 壳结构（ 5）; 并且在光刻溶液中用具有受控波长的光照射核 - 壳结构，以通过尺寸选择性光刻法在芯 - 壳结构内的壳体（3）内部形成可调节的空隙空间。 核 - 壳结构允许制备显示出非常高效率的催化剂，并且可以用作制备纳米器件所需的纳米材料的前体。