摘要:
An adhesive tape for attaching and fixing electronic components has an adhesive layer on at least one surface of a heat-resistant film. The surface hardness of the adhesive layer is about more than 25 MPa, and the surface hardness of the adhesive layer is about more than 80 MPa after thermosetting at 200° C. for about one hour.
摘要:
An adhesive tape for attaching and fixing electronic components has an adhesive layer on at least one surface of a heat-resistant film. The surface hardness of the adhesive layer is about more than 25 MPa, and the surface hardness of the adhesive layer is about more than 80 MPa after thermosetting at 200° C. for about one hour.
摘要:
This disclosure provides polymer electrolytes for dye-sensitized solar cells that can not only prevent electrolytes from leaking, but also exhibit a higher solar conversion efficiency when compared with conventional polymer electrolytes, whereby the polymer electrolytes are applicable to a process for manufacturing dye-sensitized solar cells with a large surface area or flexible dye-sensitized solar cells, and methods for manufacturing modules of dye-sensitized solar cells using the same.
摘要:
This disclosure provides polymer electrolytes for dye-sensitized solar cells that can not only prevent electrolytes from leaking, but also exhibit a higher solar conversion efficiency when compared with conventional polymer electrolytes, whereby the polymer electrolytes are applicable to a process for manufacturing dye-sensitized solar cells with a large surface area or flexible dye-sensitized solar cells, and methods for manufacturing modules of dye-sensitized solar cells using the same.
摘要:
The present invention pertains to an adhesive tape composition for electronic components used for bonding electronic components used in semiconductor devices, e.g., leads, PRH, semiconductor chips, die pads, etc. In particular, the present invention concerns an adhesive tape composition excellent in electric reliability, adhesive strength and taping workability. The adhesive tape composition according to the present invention is characterized in that it contains acrylonitrile butadiene rubber (NBR) containing the carboxyl functional group at the end thereof, epoxy resin, phenol resin and one or more sorts of hardener selected from amine and acid anhydride hardeners.
摘要:
The invention pertains to a silicone release composition of which the peeling force can be controlled and also a silicone release film coated with the composition. With the inventive composition and the release film coated with the composition, it is possible to obtain a reproducible peeling force with a given value, and also possible to produce a uniformly coated release film without discharged harmful solvent. The silicone release film produced as such can have controlled peeling force with a stable peeling force characteristic compatible with viscous agent. To this end, the invention is characterized in that the silicone release composition of which the peeling force can be controlled according to the invention is a silicone water-dispersed release coating composition, contains organopolysiloxane, organopolysiloxane resin, organo hydrogen polysiloxane and platinum chelate catalyst, and meets the following math figure for peeling force: Peeling Force=a X+b, where a=61.62±3.98, and b=16.43±3.01, X=the content(%) of organopolysiloxane resin in the release coating composition.
摘要翻译:本发明涉及可以控制剥离力的有机硅剥离组合物,以及涂覆有组合物的硅氧烷剥离膜。 利用本发明的组合物和涂布有组合物的剥离膜,可以获得具有给定值的可再现的剥离力,并且还可以生产均匀涂布的脱模膜而不排出有害溶剂。 这样制造的有机硅剥离膜可以具有受控的剥离力,具有与粘性剂相容的稳定的剥离力特性。 为此,本发明的特征在于根据本发明可以控制剥离力的有机硅剥离组合物是硅氧烷水分散剥离涂料组合物,其包含有机聚硅氧烷,有机聚硅氧烷树脂,有机氢聚硅氧烷和铂螯合催化剂, 并符合以下剥离力数学:剥离力= a X + b,其中a = 61.62±3.98,b = 16.43±3.01,X =剥离涂料组合物中有机聚硅氧烷树脂的含量(%)。
摘要:
The invention relates to an antistatic silicone release film having a layer coated with an antistatic silicone release composition, and, used for semiconductors, electronics and display devices while addressing problems of static electricity generated when a general release film is separated from adhesive or an adhesive layer, and of contamination by such static electricity that causes critical product defects. The invention also relates to an antistatic silicon release film that can reduce product contamination caused by static electricity in peeling the film from adhesive or an adhesive layer, and achieves close adhesion between a substrate and a coated layer because of no interruption in curing a release layer, and also thereby has a stable release property.
摘要:
The invention relates to an antistatic silicone release film having a layer coated with an antistatic silicone release composition, and, used for semiconductors, electronics and display devices while addressing problems of static electricity generated when a general release film is separated from adhesive or an adhesive layer, and of contamination by such static electricity that causes critical product defects. The invention also relates to an antistatic silicon release film that can reduce product contamination caused by static electricity in peeling the film from adhesive or an adhesive layer, and achieves close adhesion between a substrate and a coated layer because of no interruption in curing a release layer, and also thereby has a stable release property.
摘要:
The present invention relates to a biaxially stretched, laminated, white microporous polyester film, which can be used in a wide range of industrial applications including printing, imaging, advertising and display. The film of the present invention comprises a porous polyester resin layer B containing a thermoplastic resin non-compatible with polyester; a polyester resin-based photic layer A formed on one surface of the resin layer B, the photic layer A having a 60-degree gloss of the surface thereof of more than 100%; and an aphotic layer C formed on the other surface of the resin layer B, the aphotic layer C having a 60-degree gloss of the surface thereof of less than 50%. The total density of the photic layer A and the aphotic layer C is 0.55–1.2 g/cm3. This film has excellent gloss and flexibility so that it is very suitable for use in printing and imaging.
摘要翻译:本发明涉及双轴拉伸,层压的白色微孔聚酯薄膜,其可用于广泛的工业应用,包括印刷,成像,广告和显示。 本发明的膜包括含有与聚酯不相容的热塑性树脂的多孔聚酯树脂层B; 形成在树脂层B的一个表面上的聚酯树脂基光致发光层A,其表面的光泽度大于100%的光层A; 以及形成在树脂层B的另一个表面上的无孔层C,其表面的光泽度为60度以上的无孔层C小于50%。 光层A和无孔层C的总密度为0.55-1.2g / cm 3。 该膜具有优异的光泽度和柔韧性,因此非常适合用于印刷和成像。
摘要:
A polyester film for protecting a polarizing plate is provided wherein the polyester film includes a polyester substrate film, and an anti-static layer provided on at least one surface of the polyester substrate film, the anti-static layer coated with an anti-static coating solution comprising a conductive polymer resin, a polyurethane resin, a cross linking agent and a fluoro resin wherein the anti-static coating solution comprises, on a basis of 100 parts by weight of the conductive polymer resin, about 100 to about 1,000 parts of the polyurethane resin, about 100 to about 2000 parts of the cross linking agent and about 30 to about 300 parts of the fluoro resin.