摘要:
A composition containing an alkoxysilyl-functional polymer, a phenylsilicone resin, and a non-reactive plasticizer, when cured, exhibits very high elongation without loss of tensile strength. The compositions are particularly well suited for flexible adhesives.
摘要:
Metal catalysts employed in the preparation of organyloxysilyl-functional, moisture curable polymers, are deactivated by cheating with specific chelating agents. Compositions containing the polymers exhibit improved storage stability.
摘要:
A multi-component crosslinkable composition includes at least one component (K1) and one component (K2). Component (K1) contains organosilicon compounds (A1) selected from compounds (A1a) of formula (Ia), the formula (Ia) being Y1—[B1—CR22—SiRa(OR1)3-a]x, and compounds (A1b) of formula (Ib), the formula (Ib) being Y2—[B2—(CR42)b—Si(OR3)3]y. Component (K2), based in each case on 100 parts by weight of compounds (A1) in component (K1), includes at least 0.05 parts by weight of water and 10 to 1000 parts by weight of a component (A2) selected from compounds (A2a) of formula (IIa), the formula (IIa) being Y3—B3—CR72—SiR5c(OR6)3-c, and compounds (A2b) of formula (IIb), the formula (IIb) being Y4—[B4—(CR102)e—SiR8d(OR9)3-d]z.
摘要:
Floor coatings with improved properties are prepared from alkoxysilyl-functional polymers, silicone resins with a high alkoxy group content, and a filler component, at least a portion of which contains large particle sizes.
摘要:
Moisture-curing adhesives simultaneously having high tensile strength and elongation are prepared by admixing a silane-terminated polyurethane or polyether polymer having a defined and limited molecular weight, finely divided silica, and an organosilicon compound containing basic nitrogen.
摘要:
A crosslinkable composition comprising aminoalkyl-functional and epoxy-functional silanes and/or siloxanes provides an improvement in adhesion and sealing of various substrates under the conditions of cold-water storage, especially when a significant portion of all the silicon units has an amino-functional or an epoxy-functional unit and has an SiC-bonded, optionally halogen-substituted alkyl radical.
摘要:
A process for preparing silane-terminated polymers (SP) of the formula (I), Y—[O—C(═O)—NH—(CR12)b—SiRa(OR2)3-a]x (I), includes in a 1st process step at least one polymer (OHP) of the formula (II), Y—[OH]x (II), being reacted with at least one isocyanate-functional silane (IS) of the formula (III), O═C═N—(CR12)b—SiRa(OR2)3-a (III), with the proviso that the isocyanate-functional silanes (IS) are used in an amount such that there are at least 1.05 isocyanate groups in the silanes (IS) to each hydroxyl group in the compounds (OHP). Subsequently, in a 2nd process step, the unreacted isocyanate groups of the silanes (IS) are reacted, in the reaction mixture obtained in the 1st process step, with at least one alcohol (A) of the formula (IV), R3OH (IV) Subsequently, in a 3rd process step, the reaction mixture obtained in the 2nd process step is passed through an evaporation unit (VD).
摘要:
Crosslinkable compositions suitable for use as adhesives or sealants contain: (A) 100 parts by weight of silane-crosslinking polymers (A1) of the formula R2—O-Z1-O—CO—NH—(CH2)—SiRa(OR1)3-a (I) and/or polymers (A2) of the formula R4—O-Z2-O—CO—NH—(CH2)3—Si(OR3)3 (II), (B) 0 to 300 parts by weight of silane-crosslinking polymers having at least two end groups of the formula —SiR7c(OR8)3-c (III), and also (C) 20 to 400 parts by weight of a tackifier resin.
摘要:
Moisture curable compositions having a low modulus and a high resilience are prepared by curing a composition containing a first polymer which predominately contains two moisture-curable silyl groups, and a second polymer which is terminated by an alkoxy group and contains but a single moisture-curable silyl group, or a hydroxyl group.
摘要:
Moisture curable compositions having a low modulus and a high resilience are prepared by curing a composition containing a first polymer which predominately contains two moisture-curable silyl groups, and a second polymer which is terminated by an alkoxy group and contains but a single moisture-curable silyl group, or a hydroxyl group.