摘要:
A method for forming strained epitaxial carbon-doped silicon (Si) films, for example as raised source and drain regions for electronic devices. The method includes providing a structure having an epitaxial Si surface and a patterned film, non-selectively depositing a carbon-doped Si film onto the structure, the carbon-doped Si film containing an epitaxial carbon-doped Si film deposited onto the epitaxial Si surface and a non-epitaxial carbon-doped Si film deposited onto the patterned film, and non-selectively depositing a Si film on the carbon-doped Si film, the Si film containing an epitaxial Si film deposited onto the epitaxial carbon-doped Si film and a non-epitaxial Si film deposited onto the non-epitaxial carbon-doped Si film. The method further includes dry etching away the non-epitaxial Si film, the non-epitaxial carbon-doped Si film, and less than the entire epitaxial Si film to form a strained epitaxial carbon-doped Si film on the epitaxial Si surface.
摘要:
An in-situ hybrid film deposition method for forming a high-k dielectric film on a plurality of substrates in a batch processing system. The method includes loading the plurality of substrates into a process chamber of the batch processing system, depositing by atomic layer deposition (ALD) a first portion of a high-k dielectric film on the plurality of substrates, after depositing the first portion, and without removing the plurality of substrates from the process chamber, depositing by chemical vapor deposition (CVD) a second portion of the high-k dielectric film on the first portion, and removing the plurality of substrates from the process chamber. The method can further include alternatingly repeating the deposition of the first and second portions until the high-k dielectric film has a desired thickness. The method can still further include pre-treating the substrates and post-treating the high-k dielectric film in-situ prior to the removing.
摘要:
A method for growing an oxynitride film on a substrate includes positioning the substrate in a process chamber, heating the process chamber, flowing a first wet process gas comprising water vapor into the process chamber, and reacting the substrate with the first wet process gas to grow an oxide film on the substrate. The method further includes flowing a second wet process gas comprising water vapor and a nitriding gas comprising nitric oxide into the process chamber, and reacting the oxide film and the substrate with the second wet process gas to grow an oxynitride film. In another embodiment, the method further comprises annealing the substrate containing the oxynitride film in an annealing gas. According to one embodiment of the method where the substrate is silicon, a silicon oxynitride film can be formed that exhibits a nitrogen peak concentration of approximately 3 atomic % or greater.
摘要:
A disclosed film deposition apparatus includes a turntable having in one surface a substrate receiving portion along a turntable rotation direction; a first reaction gas supplying portion for supplying a first reaction gas; a second reaction gas supplying portion for supplying a second reaction gas; a separation area between a first process area where the first reaction gas is supplied and a second process area where the second reaction gas is supplied, the separation area including a separation gas supplying portion for supplying a first separation gas in the separation area, and a ceiling surface opposing the one surface to produce a thin space; a center area having an ejection hole for ejecting a second separation gas along the one surface; and an evacuation opening for evacuating the chamber.
摘要:
A method for performing an oxidation process on a plurality of substrates in a batch processing system. According to one embodiment, the method includes selecting a N2O-based oxidation process for the substrates including a first process gas containing N2O that thermally decomposes in a process chamber of the batch processing system to N2, O2, and NO byproducts, and generating a replacement NO-based oxidation process for the substrates including a second process gas containing N2, O2, and NO with molar concentrations that mimic that of the N2, O2, and NO byproducts in the N2O-based oxidation process. According to another embodiment of the invention, the NO-based oxidation process contains NO, O2, and an inert gas.
摘要:
An in-situ hybrid film deposition method for forming a high-k dielectric film on a plurality of substrates in a batch processing system. The method includes loading the plurality of substrates into a process chamber of the batch processing system, depositing by atomic layer deposition (ALD) a first portion of a high-k dielectric film on the plurality of substrates, after depositing the first portion, and without removing the plurality of substrates from the process chamber, depositing by chemical vapor deposition (CVD) a second portion of the high-k dielectric film on the first portion, and removing the plurality of substrates from the process chamber. The method can further include alternatingly repeating the deposition of the first and second portions until the high-k dielectric film has a desired thickness. The method can still further include pre-treating the substrates and post-treating the high-k dielectric film in-situ prior to the removing.
摘要:
A method is provided for oxide removal from a substrate. The method includes providing the substrate in a process chamber where the substrate has an oxide layer formed thereon, and performing a sequential oxide removal process. The sequential oxide removal process includes exposing the substrate at a first substrate temperature to a flow of a first etching gas containing F2 to partially remove the oxide layer from the substrate, raising the temperature of the substrate from the first substrate temperature to a second substrate temperature, and exposing the substrate at the second temperature to a flow of a second etching gas containing H2 to further remove the oxide layer from the substrate. In one embodiment, a film may be formed on the substrate following the sequential oxide removal process.
摘要:
A method for growing an oxynitride film on a substrate includes positioning the substrate in a process chamber, heating the process chamber, flowing a wet process gas comprising water vapor and a nitriding gas comprising nitric oxide into the process chamber. The wet process gas and the nitriding gas form a processing ambient that reacts with the substrate such that an oxynitride film grows on the substrate. In yet another embodiment, the method further comprises flowing a diluting gas into the process chamber while flowing the wet process gas to control a growth rate of the oxynitride film. In another embodiment, the method further comprises annealing the substrate and the oxynitride film in an annealing gas. According to embodiments of the method where the substrate is silicon, a silicon oxynitride film forms that exhibits a nitrogen peak concentration of at least approximately 6 atomic % and an interface state density of less than approximately 1.5×1012 per cc.
摘要:
Systems and methods for depositing thin films using Atomic Layer Deposition (ALD). The deposition system includes a process chamber with a peripheral sidewall, partitions that divide a processing space inside the process chamber into at least first and second compartments, and a platter that supports substrates within the processing space. The platter rotates the substrates relative to the stationary peripheral sidewall and compartments. The first compartment receives a process material used to deposit a layer on each of the substrates. An injector, which injects the process material, communicates with the first compartment through the peripheral sidewall.
摘要:
A method and system for processing a substrate includes providing the substrate in a process chamber, the substrate having an oxide layer formed thereon, and exposing the substrate to an etching gas containing F2 gas at a first temperature to remove the oxide layer from the substrate. The substrate may subsequently be heated to a second temperature greater than the first temperature, and a film may then be formed on the substrate at the second temperature. In one embodiment, a Si film is epitaxially formed on a Si substrate.