摘要:
A TFT formed on an insulating substrate source, drain and channel regions, a gate insulating film formed on at least the channel region and a gate electrode formed on the gate insulating film. Between the channel region and the drain region, a region having a higher resistivity is provided in order to reduce an Ioff current. A method for forming this structure comprises the steps of anodizing the gate electrode to form a porous anodic oxide film on the side of the gate electrode; removing a portion of the gate insulating using the porous anodic oxide film as a mask so that the gate insulating film extends beyond the gate electrode but does not completely cover the source and drain regions. Thereafter, an ion doping of one conductivity element is performed. The high resistivity region is defined under the gate insulating film.
摘要:
A TFT formed on an insulating substrate source, drain and channel regions, a gate insulating film formed on at least the channel region and a gate electrode formed on the gate insulating film. Between the channel region and the drain region, a region having a higher resistivity is provided in order to reduce an Ioff current. A method for forming this structure comprises the steps of anodizing the gate electrode to form a porous anodic oxide film on the side of the gate electrode; removing a portion of the gate insulating using the porous anodic oxide film as a mask so that the gate insulating film extends beyond the gate electrode but does not completely cover the source and drain regions. Thereafter, an ion doping of one conductivity element is performed. The high resistivity region is defined under the gate insulating film.
摘要:
An anodic oxide containing impurities at a low concentration and thereby improved in film quality, and a process for fabricating the same. The process comprises increasing the current between a metallic thin film and a cathode until a voltage therebetween reaches a predetermined value, and maintaining the voltage at the predetermined value thereafter.
摘要:
An etching material comprising at least phosphoric acid, acetic acid, and nitric acid, with chromic acid added therein. Also claimed is an etching process using the etching material above, provided that the process comprises selectively etching, by using the solution, an aluminum oxide layer formed on the surface of a material containing aluminum as the principal component thereof.
摘要:
An anodic oxide containing impurities at a low concentration and thereby improved in film quality, and a process for fabricating the same. The process comprises increasing the current between a metallic thin film and a cathode until a voltage therebetween reaches a predetermined value, and maintaining the voltage at the predetermined value thereafter.
摘要:
A TFT formed on an insulating substrate source, drain and channel regions, a gate insulating film formed on at least the channel region and a gate electrode formed on the gate insulating film. Between the channel region and the drain region, a region having a higher resistivity is provided in order to reduce an Ioff current. A method for forming this structure comprises the steps of anodizing the gate electrode to form a porous anodic oxide film on the side of the gate electrode; removing a portion of the gate insulating using the porous anodic oxide film as a mask so that the gate insulating film extends beyond the gate electrode but does not completely cover the source and drain regions. Thereafter, an ion doping of one conductivity element is performed. The high resistivity region is defined under the gate insulating film.
摘要:
An alumina film, a silicon oxide film, and a silicon nitride film formed on a substrate containing a large amount of alumina are etched by using an etching material in which the concentration of ammonium fluoride, which is a component of BHF, is set low. Etching is performed by using an etching material that is an aqueous solution produced by mixing hydrofluoric acid, ammonium fluoride and water at a weight ratio of x:y:(100-x-y) where x and y satisfy a relationship y
摘要:
A thin film transistor according to this invention has a gate electrode comprising a lower layer of aluminum of a high purity of over 99.5% and an upper layer of aluminum containing over 0.5% silicon. Alternatively, it has a gate electrode made by adding a IIIa group element to a IIIb group element. Residues produced by the etching of the silicon-containing aluminum gate electrode are etched with a mixture solution of hydrofluoric acid, nitric acid and acetic acid. After contact holes have been formed in an interlayer insulating film, laser annealing is carried out, and metal electrodes are formed in the contact holes thereafter.
摘要:
A TFT formed on an insulating substrate source, drain and channel regions, a gate insulating film formed on at least the channel region and a gate electrode formed on the gate insulating film. Between the channel region and the drain region, a region having a higher resistivity is provided in order to reduce an Ioff current. A method for forming this structure comprises the steps of anodizing the gate electrode to form a porous anodic oxide film on the side of the gate electrode; removing a portion of the gate insulating using the porous anodic oxide film as a mask so that the gate insulating film extends beyond the gate electrode but does not completely cover the source and drain regions. Thereafter, an ion doping of one conductivity element is performed. The high resistivity region is defined under the gate insulating film.
摘要:
A TFT formed on an insulating substrate source, drain and channel regions, a gate insulating film formed on at least the channel region and a gate electrode formed on the gate insulating film. Between the channel region and the drain region, a region having a higher resistivity is provided in order to reduce an Ioff current. A method for forming this structure comprises the steps of anodizing the gate electrode to form a porous anodic oxide film on the side of the gate electrode; removing a portion of the gate insulating using the porous anodic oxide film as a mask so that the gate insulating film extends beyond the gate electrode but does not completely cover the source and drain regions. Thereafter, an ion doping of one conductivity element is performed. The high resistivity region is defined under the gate insulating film.