摘要:
Processes for the production of tantalum alloys and niobium are disclosed. The processes use aluminothermic reactions to reduce tantalum pentoxide to tantalum metal or niobium pentoxide to niobium metal.
摘要:
A friction member for a bicycle brake that is obtained through combustion synthesis is disclosed. One example of the bicycle brake friction member includes an intermetallic compound, which is obtained from a first metal and a second metal, and a metal phase, which is obtained from the first metal.
摘要:
A general procedure applied to a variety of sol-gel precursors and solvent systems for preparing and controlling homogeneous dispersions of very small particles within each other. Fine homogenous dispersions processed at elevated temperatures and controlled atmospheres make a ceramic powder to be consolidated into a component by standard commercial means: sinter, hot press, hot isostatic pressing (HIP), hot/cold extrusion, spark plasma sinter (SPS), etc.
摘要:
Processes for the production of tantalum alloys and niobium are disclosed. The processes use aluminothermic reactions to reduce tantalum pentoxide to tantalum metal or niobium pentoxide to niobium metal.
摘要:
A sintering film comprising one or more metals, one or more metal alloys, or blends of one or more metals and one or more metal alloys, is prepared optionally using a solid or semi-solid organic binder. The organic binder can have fluxing functionality; the organic binder can be one that will partially or completely decompose upon sintering of the metal or metal alloy in the composition. In one embodiment, the sintering film is provided on an end use substrate, such as a silicon die or wafer, or a metal circuit board or foil, or the sintering film is provided on a carrier, such as a metal mesh. Preparation is accomplished by dispersing the metal or metal alloy in a suitable solvent, with or without a binder, and exposing the composition to high temperature to evaporate off the solvent and partially sinter the metal or metal alloy.
摘要:
Disclosed herein is a method of manufacturing inorganic hollow yarns, such as cermets, oxide-non oxide composites, poorly sinterable non-oxides, and the like, at low costs. The method includes preparing a composition comprising a self-propagating high temperature reactant, a polymer and a dispersant, wet-spinning the composition through a spinneret to form wet-spun yarns, washing and drying the wet-spun yarns to form polymer-self propagating high temperature reactant hollow yarns, and heat-treating the polymer-self propagating high temperature reactant hollow yarns to remove a polymeric component from the polymer-self propagating high temperature reactant hollow yarns while inducing self-propagating high temperature reaction of the self-propagating high temperature reactant to form inorganic hollow yarns. The composition comprises 45˜60 wt % of the self-propagating high temperature reactant, 6˜17 wt % of the polymer, 0.1˜4 wt % of the dispersant, and the balance of an organic solvent.
摘要:
Disclosed herein is a method of manufacturing inorganic hollow yarns, such as cermets, oxide-non oxide composites, poorly sinterable non-oxides, and the like, at low costs. The method includes preparing a composition comprising a self-propagating high temperature reactant, a polymer and a dispersant, wet-spinning the composition through a spinneret to form wet-spun yarns, washing and drying the wet-spun yarns to form polymer-self propagating high temperature reactant hollow yarns, and heat-treating the polymer-self propagating high temperature reactant hollow yarns to remove a polymeric component from the polymer-self propagating high temperature reactant hollow yarns while inducing self-propagating high temperature reaction of the self-propagating high temperature reactant to form inorganic hollow yarns. The composition comprises 45˜60 wt % of the self-propagating high temperature reactant, 6˜17 wt % of the polymer, 0.1˜4 wt % of the dispersant, and the balance of an organic solvent.
摘要:
The present invention relates to coated powder, comprising a Ti-bearing core and a Ni-bearing coating, which can be used for the production of porous Ni—Ti articles by the self-propagating high temperature synthesis (SHS) method. The obtained articles are ideally suited for use in biomedical applications. According to the invention, a coated powder is used comprising a metallic Ti-bearing core and a metallic Ni-bearing coating, characterised by a Ni:Ti atomic ratio of more than 0.5, preferably between 0.9 and 1.1, and more preferably between 0.96 and 1.04. By using coated powders, local fluctuations in composition are limited and well under control. Milling of powders and the ensuing contamination risks are avoided. The sintered objects obtained using coated powders have a more homogeneous porosity than that using mixed Ni and Ti powders.
摘要:
This invention provides novel thermoelectric compounds comprising: a) atomic percent Ytterbium b) between 50 and 74.999 atomic percent Aluminum c) between 0.001 and 25 atomic percent Manganese and a process for their preparation.
摘要:
W powders and C powders are mixed at a ratio of 1:1, the raw material mixed powder is compacted to prepare a formed body, the formed body is embedded into a powder mixture capable of performing combustion synthesis, a part of the powder mixture is powerfully heated to ignite the part and perform combustion synthesis, and according to heat of formation released, a reaction represented by W+C→WC is induced and the reaction is subjected to combustion synthesis to convert a whole of the formed body into sintered WC.