摘要:
An epoxy resin composition is provided that mainly comprises an epoxy resin, a curing agent, and an inorganic filler, and that cures into a product having a coefficient of water diffusion of up to 1.times.10.sup.-4 cm.sup.2 /hr. at a thickness of 3 mm under humid conditions at 85.degree. C. and RH 85%, wherein 1-50% by weight of an inorganic water absorbing agent such as molecular sieve, silica gel and porous silica is added to the epoxy resin composition. The composition offers cured products having fully low moisture permeability and is thus suitable as a pre-molded hollow package-forming material.
摘要翻译:提供了一种环氧树脂组合物,其主要包括环氧树脂,固化剂和无机填料,并且固化成具有高达1×10 -4 cm 2 / hr的水扩散系数的产物。 在湿度条件为85℃,RH为85%的条件下,在环氧树脂组合物中加入1-50重量%的无机吸水剂如分子筛,硅胶和多孔二氧化硅。 该组合物提供具有完全低透湿性的固化产物,因此适合作为预成型的中空包装形成材料。
摘要:
A epoxy resin composition comprising (A) an epoxy resin bearing at least one monovalent hydrocarbon group on a benzene ring, (B) a phenolic resin, (C) an inorganic filler, and (D) 2-phenyl-4,5-dihydroxymethylimidazole as a curing accelerator has a low melt viscosity, a long gel time and a high curing rate, and provides cured products having improved properties. Semiconductor devices encapsulated with cured products of the inventive composition are reliable.
摘要:
A novel quaternary phosphorus compound is a salt between tetraphenyl borate and a phosphonium having an aromatic group attached to a phosphorus atom through an oxygen atom. It is blended with an epoxy resin as a curing catalyst to form an epoxy resin composition which flows smoothly and quickly cures into a product having improved moisture resistance and adhesion.
摘要:
In a light transmissive epoxy resin composition comprising (A) an epoxy resin and (B) a curing agent are blended (C) an organic phosphorus anti-discoloring agent and (D) silica-titania glass beads surface treated with an organic silicon compound. The composition restrains coloring in composition form and discoloration in cured form while curing into clear low stressed products having high light transmittance. Optical semiconductor devices encapsulated with the cured epoxy resin composition are reliable.
摘要:
An epoxy resin composition contains (A) an epoxy resin, (B) a curing agent, (C) an inorganic filler, and (D) catalyzed microcapsules containing an imidazole compound or organic phosphorus compound and having a mean particle size of 0.5-50 &mgr;m, the quantity of the catalyst leached out from the microcapsules in o-cresol at 30° C. for 15 minutes being at least 70% by weight of the entire catalyst quantity. The composition is suited for semiconductor package encapsulation since it has satisfactory catalyst latency, storage stability and cure.
摘要:
In an epoxy resin composition comprising an epoxy resin, a curing agent, and an inorganic filler, the filler is porous silica having a specific surface area of 6-200 m2/g, a true specific gravity of 2.0-2.2, and a mean particle size of 2-50 &mgr;m. The epoxy resin composition is readily moldable, has a low moisture permeability and reliability in the cured state, and is suitable for forming a premolded hollow semiconductor package.
摘要:
Epoxy resin compositions comprising (A) a crystalline epoxy resin, (B) a polyfunctional phenolic resin, (C) an organic phosphorus curing accelerator, (D) an aminosilane coupling agent, and (E) at least 88 wt % based on the composition of an inorganic filler are smoothly flowing, fast curing and shelf stable. Due to minimized package warp, minimized wire flow, improved adhesion, and low water absorption, the compositions enable highly reliable encapsulation of semiconductor devices, especially BGA.
摘要:
Epoxy resin compositions comprising (A) a polyfunctional epoxy resin, (B) a polyfunctional phenolic resin curing agent, (C) an organophosphorus curing accelerator, (D) an aminosilane coupling agent, and (E) an inorganic filler have excellent flow properties, shelf stability and curing speed and are thus suitable for semiconductor encapsulation, especially BGA encapsulation. Semiconductor devices encapsulated with the epoxy resin compositions are highly reliable.
摘要:
Novel fluorine-modified acid anhydrides of formula (1) are useful curing agents typically in epoxy resin compositions for encapsulating semiconductor devices. ##STR1## R.sup.1 is a hydrogen atom, substituted or unsubstituted monovalent hydrocarbon group, hydroxyl group, alkoxy group or alkenyloxy group. Rf is a divalent perfluoroalkylene or perfluoropolyether group of the general formula (2): ##STR2## wherein l is an integer of 0 to 8, k and m are integers of 0 to 15, j and n are 0 or 1, with the proviso that j, k, l, m and n are not equal to 0 at the same time.
摘要:
In an epoxy resin composition comprising an epoxy resin, a curing agent, and an inorganic filler, the filler is porous silica having a specific surface area of 6-200 m2/g, a true specific gravity of 2.0-2.2, and a mean particle size of 2-50 &mgr;m. The epoxy resin composition is readily moldable, has a low moisture permeability and reliability in the cured state, and is suitable for forming a premolded hollow semiconductor package.