Abstract:
According to some embodiments a method of processing an optical fiber comprises the steps of: (i) drawing the fiber at a drawing rate of at least 30 m/sec; and (ii) cooling the drawn fiber in a gas at an average cooling rate less than 5000 °C/s, such that said cooling reduces the temperature of the fiber from an entering temperature in the range between 1500 °C and 1700 °C to another temperature in the range between 1200 °C and 1400 °C, the gas being at a temperature between 800 °C and 1500 °C; and the thermal conductivity K of the gas being not greater than 1.5xl0" 4 cal/cm-s-K for at least one temperature within a range of 800 °C to 1500 °C at one atm (atmosphere) pressure absolute.
Abstract:
Annealing treatments for modified titania-silica glasses and the glasses produced by the annealing treatments. The annealing treatments include an isothermal hold that facilitates equalization of non-uniformities in fictive temperature caused by non-uniformities in modifier concentration in the glasses. The annealing treatments may also include heating the glass to a higher temperature following the isothermal hold and holding the glass at that temperature for several hours. Glasses produced by the annealing treatments exhibit high spatial uniformity of CTE, CTE slope, and fictive temperature, including in the presence of a spatially non-uniform concentration of modifier.
Abstract:
Die vorliegende Erfindung betrifft ein Substrat für einen EUV-Spiegel, das einen von der statistischen Verteilung abweichenden Verlauf der Nulldurchgangstemperatur aufweist. Weiterhin betrifft die Erfindung ein Verfahren zur Herstellung eines Substrates für einen EUV-Spiegel und dessen Verwendung, wobei der Verlauf der Nulldurchgangstemperatur im Substrat der Betriebstemperatur des Spiegels angepasst ist sowie ein Lithographieverfahren unter Verwendung eines solchen Substrates.
Abstract:
The present disclosure is directed to a doped silica-titania glass, DST glass, consisting essentially of 0.1 wt.% to 5 wt.% halogen, 50 ppm-wt. to 6 wt.% of one or more oxides of Al, Ta and Nb, 3 wt.% to 10 wt.% TiO 2 and the remainder SiO 2 . In an embodiment the halogen content can be in the range of 0.2 wt.% to 3 wt.% along with 50 ppm-wt. to 6 wt.% one or more oxides of Al, Ta and Nb, 3 wt.% to 10 wt.% TiO 2 and the remainder SiO 2 . In an embodiment the DST glass has an OH concentration of less than 100 ppm. In another embodiment the OH concentration is less than 50 ppm. The DST glass has a Active temperature T f of less than 875°C. In an embodiment T f is less than 825°C. In another embodiment T f is less than 775°C.
Abstract:
Für die Herstellung zylinderförmiger Bauteile aus Fluor enthaltendem, synthetischem Quarzglas sind folgende Verfahrensschritte bekannt: Erzeugen eines SiO 2 - Sootkörpers; Entfernen von Hydroxylgruppen aus dem Sootkörper, Beladen des Sootkörpers mit Fluor, Nachchlorieren des mit Fluor beladenen Sootkörpers und Verglasen des Sootkörpers zu dem zylinderförmigen Bauteil. Um reproduzierbar axial und radial besonders homogene Verteilungen insbesondere von Fluor zu erreichen, wird erfindungsgemäß vorgeschlagen, dass beim Trocknen im Sootkörper eine Konzentration an Hydroxylgruppen im Bereich von 1 bis 300 Gew.-ppm und beim Beladen mit Fluor ein mittlerer Fluorgehalt von mindestens 1500 Gew.-ppm eingestellt wird, und dass beim Nachchlorieren eine Beladung mit Chlor erfolgt, die nach dem Verglasen im synthetischen Quarzglas des Bauteils einen mittleren Chlorgehalt von mindestens 50 Gew.-ppm ergibt, unter der weiteren Maßgabe, dass das Gewichtsverhältnis der Gehalte von Fluor und Chlor kleiner als 30 ist.
Abstract:
Bekannt ist ein Quarzglasrohr als Halbzeug für ein optisches Bauteil, das eine sich entlang einer Rohr-Mittelachse erstreckende Innenbohrung zur Aufnahme eines Kernstabs und eine von einer Innenmantelfläche und einer Außenmantelfläche begrenzte Rohrwandung aufweist, in der ein innerer Bereich aus einem ersten Quarzglas und ein den inneren Bereich umgebender äußerer Bereich aus einem zweiten Quarzglas an einer Kontaktfläche aneinander liegen, die um die Mittelachse verläuft, wobei sich die Brechungsindizes von ersten und zweitem Quarzglas unterscheiden. Um hiervon ausgehend ein Quarzglasrohr bereitzustellen, das die Herstellung optischer Bauteile für Spezialanwendungen, wie laseraktive optische Bauteile in Stab- oder Faserform erleichtert, wird erfindungsgemäß vorgeschlagen, dass die Kontaktfläche im radialen Querschnitt einen nicht-runden Verlaufund die Innenmantelfläche einen kreisrunden Verlauf zeigen.