摘要:
The present invention provides a substrate for a flexible printed wiring board including an adhesive layer containing an epoxy resin composition, insulating layers respectively stacked on both sides of the adhesive layer and formed with a pair of films containing a nonthermoplastic polyimide resin, and conductor layers respectively disposed on the outer surfaces of the films. The total thickness of the insulating layers respectively stacked on both sides of the adhesive layer is 10 to 100 μm and 2 to 10 times the thickness of the adhesive layer. The mutual adhesion strength between the insulating layers through the intermediary of the adhesive layer is 7.0 N/cm or more.
摘要:
The present invention provides a substrate for a flexible printed wiring board including an adhesive layer containing an epoxy resin composition, insulating layers respectively stacked on both sides of the adhesive layer and formed with a pair of films containing a nonthermoplastic polyimide resin, and conductor layers respectively disposed on the outer surfaces of the films. The total thickness of the insulating layers respectively stacked on both sides of the adhesive layer is 10 to 100 μm and 2 to 10 times the thickness of the adhesive layer. The mutual adhesion strength between the insulating layers through the intermediary of the adhesive layer is 7.0 N/cm or more.
摘要:
A method for preparing a substrate for a flexible print wiring board having a polyimide based resin layer wherein a solution of a polyimide based resin precursor is directly applied on an electrically conducting material to form a polyimide based resin precursor layer and then the precursor layer is cured by heating to prepare a polyimide based resin layer, characterized in that a solution of a polyimide based resin precursor B, which is one of solutions of two types of polyimide based resin precursors, is directly applied on an electrically conducting material and then, on the resultant layer is applied a solution of a polyimide based resin precursor A which allows resolving the residual strain generated in the polyimide based resin formed by the curing of the above polyimide based resin precursor B.
摘要:
A process for producing a microparticulate hardening catalyst, comprising the steps of jetting a liquid composition containing epoxy resin hardening catalyst (A), monomer having an ethylenically unsaturated group (B) and photopolymerization initiator (C) through a minute nozzle into a gas so as to form microparticles; and while the microparticles are floating, irradiating the same with high-energy rays to thereby effect polymerization of the monomer having an ethylenically unsaturated group (B).
摘要:
The present invention relates to a phenolic hydroxy group-containing rubber-modified polyamide resin which has, in the molecule, a phenolic hydroxy group-containing aromatic polyamide segment having a structure represented by the following formula (A) (wherein, m and n are average values and Ar represents a divalent aromatic group) and a butadiene (co)polymer segment selected from the following formula (B-1) or (B-2), —(CH2—CH═CH—CH2)X— (B-1) —(CH2—CH═CH—CH2)Y—(CH2—CH(CN))Z— (B-2) (wherein, each of x, y and z is an average value and 0.01≦z/(y+z)≦0.13, x represents a positive number of 5 to 200, and also y+z is a positive number of 10 to 200), and a resin composition containing said resin, in particular an epoxy resin composition; a cured product of said epoxy resin composition is excellent in flexibility, heat resistance and electrical properties especially at high temperature and high humidity.
摘要翻译:本发明涉及一种含酚羟基的橡胶改性聚酰胺树脂,其分子中含有具有由下式(A)表示的结构的含酚羟基的芳族聚酰胺链段(其中m和n分别为 平均值,Ar表示二价芳族基团)和选自下式(B-1)或(B-2)的丁二烯(共)聚合物链段,<?在线公式描述=“在线公式” 末端=“铅”→>(CH2-CH-CH-CH2)X-(B-1)<?在线公式描述=“在线公式”end =“tail”?> - (CH2-CH-CH-CH2)Y-(CH2-CH(CN))Z-(B-2)<?line line line line line line -formulae description =“In-line Formulas”end =“tail”?>(其中,x,y和z各自为平均值,0.01 <= z /(y + z)<= 0.13,x表示正数 数量为5〜200,y + z为10〜200的正数),以及含有所述树脂,特别是环氧树脂组合物的树脂组合物; 所述环氧树脂组合物的固化物的柔软性,耐热性和电特性优异,特别是在高温高湿下。
摘要:
A process for producing a microparticulate hardening catalyst, comprising the steps of jetting a liquid composition containing epoxy resin hardening catalyst (A), monomer having an ethylenically unsaturated group (B) and photopolymerization initiator (C) through a minute nozzle into a gas so as to form microparticles; and while the microparticles are floating, irradiating the same with high-energy rays to thereby effect polymerization of the monomer having an ethylenically unsaturated group (B).
摘要:
Disclosed is a heat-resistant adhesive including: a phenolic hydroxy group-containing aromatic polyamide resin (A) having a structure represented by the following formula (1) (in the formula, m and n each represent an average and satisfy the relation: 0.005≦n/(m+n)
摘要:
The invention relates to an epoxy resin composition containing (a) an epoxy resin and (b) a phenolic hydroxy group-containing polyamide resin having the structure represented by Formula (1), a method of curing the composition, a varnish, prepreg, or sheet using the composition, and an epoxy resin composition having the polyamide resin represented by Formula (1) as the active component. Cured products of the epoxy resin composition according to the present invention have a sufficient high flexibility when formed into a thin film, have a flame resistance even though the cured compositions do not contain a halogen flame retardant, an antimony compound, or the like and are superior in heat resistance and adhesiveness, and thus are extremely useful in a wide range of applications, for example, as molded materials, cast materials, laminate materials, paints, adhesives, resists, and the like. (wherein, 1 and m are averages, satisfying the formula: m/(1+m) =0.01; and 1+m is a positive number of 2 to 200. Ar1 represents a bivalent aromatic group; Ar2 represents a phenolic hydroxyl group-containing bivalent aromatic group; and Ar3 represents: -ph(R1)n- or -ph(R2)n-X-ph(R3)n-, wherein, -ph(R1)n-, -ph(R2)n- and -ph(R3)n- represent respectively R1-substituted, R2-substituted and R3-substituted phenylene groups, or an unsubstituted phenylene group; n is an integer of 0 to 3; R1, R2 and R3 each independently represent a C1 to C3 alkyl group or a C1 to C3 alkoxy group; and X represents O, S, CO, SO2 or a single bond)
摘要:
The present invention relates to a fiber comprising a heat curable polyamide resin composition containing both a) a phenolic hydroxy group-containing polyamide and b) an epoxy resin having two or more epoxy groups in one molecule, a nanofiber comprising said resin composition obtained by electrospinning method, a nonwoven fabric obtained by applying heat treatment to a laminate of said nanofiber, a method for producing said nanofiber by electrospinning method and a heat curable polyamide resin composition for fiber. A nonwoven fabric can be obtained only by subjecting a deposit of the nanofiber obtained by electrospinning method to heat treatment, nanofibers in the obtained nonwoven fabric are bonded to each other by heat-curing, and the nonwoven fabric has such characteristics that its mechanical strength, heat resistance and chemical resistance are excellent and that it has a high strength.
摘要:
The present invention relates to a phenolic hydroxy group-containing rubber-modified polyamide resin which has, in the molecule, a phenolic hydroxy group-containing aromatic polyamide segment having a structure represented by the following formula (A) (wherein, m and n are average values and Ar represents a divalent aromatic group) and a butadiene (co)polymer segment selected from the following formula (B-1) or (B-2), —(CH2—CH═CH—CH2)X— (B-1) —(CH2—CH═CH—CH2)Y—(CH2—CH(CN))Z— (B-2) (wherein, each of x, y and z is an average value and 0.01≦z/(y+z)≦0.13, x represents a positive number of 5 to 200, and also y+z is a positive number of 10 to 200), and a resin composition containing said resin, in particular an epoxy resin composition; a cured product of said epoxy resin composition is excellent in flexibility, heat resistance and electrical properties especially at high temperature and high humidity.