摘要:
The present invention provides a composite film containing polyethylene terephthalate, which comprises inorganic mineral powder, polyethylene terephthalate, an auxiliary plastic, and an auxiliary agent. The present invention also provides a method of preparing the composite film, which comprises internally mixing inorganic mineral powder, polyethylene terephthalate, an auxiliary plastic, and an auxiliary agent to form a composite soft material; configuring the composite soft material to be in a sheet shape; and stretching the composite soft material to form a composite film.
摘要:
A roofing tile composed of concrete material and a method for producing such a roofing tile. The concrete material contains a binder, a gravel, a light-weight aggregate, and added water. The roofing tile has at least one watercourse and a lateral interlocking joint having a covering fold and a water fold. The ratio of water to binder is less than 0.3, the light-weight aggregate is composed of a material that is hydrophobic and/or not hygroscopic, and the roofing tile has a density in the range of 1.6 g/cm3 to 1.9 g/cm3 after the hardening. The roofing tile has a thickness of 5 mm to 9 mm, preferably 7 mm to 8 mm, in the highly loaded regions, preferably in the region of the watercourse.
摘要:
An extrudable cement-based material is formed from a mixture that includes cement in the range of about 40 to 90% by wet weight percent, a lightweight expanded aggregate in the range of about 10 to 60% by wet weight percent, a secondary material in the range of about 0.1 to 50% by wet weight percent, a reinforcement fiber in the range of about 1 to 20% by wet weight percent, a rheology modifying agent in the range of about 0.5 to 10% by wet weight percent, a retarder in the range of about 0.1 to 8% by wet weight percent, and water in the range of 10 to 60% of a total wet material weight.
摘要:
Water filtration media having a charged material affixed directly to binder material used in the fabrication of the filter media. A microbiological interception enhancing agent is added to the binder directly. The media having a charged material and a microbiological interception enhancing agent both affixed directly on or in a binder material is then combined with core filter media and prepared as a filtration media. A filter is prepared from the treated filter media.
摘要:
Glass-fiber-reinforced concrete compositions that may be sprayed, and methods of preparing and applying such compositions. Such compositions may include cement, reinforcing glass fibers randomly oriented and homogenously distributed throughout the concrete composition, and a particle packing aggregate. At least a portion of the particle packing aggregate may be rounded rather than crushed and include a first aggregate portion having a first particle size and a second aggregate portion having a second particle size that is smaller than the first particle size so that the aggregate is capable of particle packing. The uncured compositions can be delivered through a spray nozzle with the glass fibers already mixed into the composition. The compositions can provide uniform, non-directional strength characteristics, e.g., modulus of rupture of at least 16 MPa and a limit of proportionality of at least 7 MPa with a glass-fiber content of no more than 4% by weight.
摘要:
The invention is directed to a plastic fiber article of manufacture having composite-like high strength characteristics. The article of manufacture can be in the form of a panel or board. The panel or board is constructed from low cost fiber materials, industrial grade or high thermoplastic, and other additives to protect the board or panel from ultraviolet light, fugii growth, excessive heat, fire, insect infestation, and/or weathering. The plastic fiber panel or board may be textured and colored to resemble natural wood such as cedar, walnut, or oak. The plastic fiber panel or board is stronger more durable and may be cheaper than natural wood alternative panels or boards.
摘要:
The invention relates to synthetic hybrid rock compositions, articles of manufacture and related processes employing mineral waste starting materials such as mine tailings, mine development rock, ash, slag, quarry fines, and slimes, to produce valuable articles of manufacture and products, which are characterized by superior physical and structural characteristics, including low porosity, low absorption, increased strength and durability, and retained plasticity. The resulting materials are compositionally and chemically distinct from conventional synthetic rock materials as demonstrated by scanning electron microprobe analysis, and are useful in a wide variety of applications, particularly with respect to commercial and residential construction.
摘要:
A ceramic precursor batch composition comprising inorganic ceramic-forming ingredients, a binder, an aqueous solvent and a heteroatom polyol agent. The heteroatom polyol agent can be represented by X(R) where X is at least one of S, N, and P, and R is at least two of CH3, CH2CH2OH, CH2CH2CH2OH, CH2(CHOH)CH3, C(CH2OH)1-3, CH2OH, CH(CH2OH)CHOH, C(O)(CHOH)1-4CH2OH, and CH2CH2CH2OCH3. The presence of the heteroatom polyol agent provides a composition with a lower viscosity and/or a greater batch stiffening temperature (Tonset) allowing for increased rates of extrusion. Methods for producing a ceramic honeycomb body using this ceramic precursor batch composition are also provided.
摘要:
Water filtration media having a charged material affixed directly to binder material used in the fabrication of the filter media. A microbiological interception enhancing agent is added to the binder directly. The media having a charged material and a microbiological interception enhancing agent both affixed directly on or in a binder material is then combined with core filter media and prepared as a filtration media. A filter is prepared from the treated filter media.
摘要:
The invention relates to a hydraulic binder product [12, 10] which includes a mixture of a hydraulic binder [38, 202], a polyvinyl alcohol [14, 204] and a gelling agent [54] which reacts with the polyvinyl alcohol and a method [8] of producing same.