摘要:
This invention relates to monodisperse cross-linked polymer particles, comprising particles with a substantially smooth outer surface and an average diameter of less than 1 μm, wherein the particles are solid or porous, and wherein the coefficient of variation (CV) % of the particles, when measured by CPS disk centrifugation analysis, is less than 15%. These monodisperse cross-linked polymer particles may comprise magnetic material and are useful in various application. This invention also relates to monodisperse polymer particles for use as seed particles in the Ugelstad process.
摘要:
The present invention relates to a super absorbent resin, and the super absorbent resin can exhibit a fast absorption rate and high gel strength even in a partially swollen state through the size optimization of partially swollen gel particles. Therefore, the use of the super absorbent resin can effectively prevent a rewetting phenomenon.
摘要:
A method for producing a polymer nanofoam includes: immersing a polymer material in carbon dioxide at a pressure greater than 5 MPa and a temperature of −30° C. to 40° C. to obtain a carbon dioxide-saturated polymer material, wherein the melt index of the polymer material measured at 230 ° C. and 3.8 kg is between 0.1 g/10 min and 8.0 g/10 min. Thereafter, the carbon dioxide-saturated polymer material is depressurized to atmospheric pressure, and then the carbon dioxide-saturated polymer material is heated to form the polymer nanofoam.
摘要:
A particulate polyamide is provided. The particulate polyamide is porous and includes at least one of polyamide 4 and polyamide 3. In addition, the particulate polyamide has a particle diameter (d50) of from 10 μm to 1,000 μm and a particle diameter dispersion degree (Dv/Dn) of not greater than 3.0, wherein Dv represents the volume average particle diameter of the particulate polyamide, and Dn represents the number average particle diameter of the particulate polyamide.
摘要:
Provided is a process for efficiently producing heat-expandable microspheres having high solvent resistance. The process produces the heat-expandable microspheres composed of a shell of a thermoplastic resin and a blowing agent encapsulated therein and vaporizable by heating, and includes the steps of preparing an aqueous suspension by dispersing an oily mixture containing a polymerizable component, the blowing agent, and a polymerization initiator containing, as an essential component, a peroxide A having a theoretical active oxygen content of at least 7.8%, and polymerizing the polymerizable component in the oily mixture.
摘要:
Expandable-polymer-particle material comprising at least one thermoplastic polyurethane (TPU) with Vicat softening point (in accordance with ISO 306/ASO) below 80° C. and from 5 to 95% by weight of at least one polymer obtainable via free-radical polymerization, based on the entirety of TPU and of the polymer obtainable via free-radical polymerization, where the polymer obtainable via free-radical polymerization has been bonded to the TPU in a manner that gives a comb polymer, graft polymer, or copolymer, is suitable for the production of moldings, in particular for use as insulation material.
摘要:
The present invention provides porous resin particles made of a polymer of a monomer mixture, wherein the monomer mixture contains, as monomers, at least methyl methacrylate and a (meth)acrylic-based cross-linkable monomer, a content of the methyl methacrylate in the monomer mixture is 1 to 50% by weight, a content of the (meth)acrylic-based cross-linkable monomer in the monomer mixture is 50 to 99% by weight, the porous resin particles have a specific surface area of 130 to 180 m2/g, a pore volume of 0.3 to 0.7 ml/g, and an average pore size of 13 to 16 nm, an amount of unreacted methyl methacrylate remaining in the porous resin particles is 20 ppm or less, and the porous resin particles have a thermal decomposition starting temperature of 260° C. or more.
摘要:
A method of forming a particle includes, in a disperse phase within an aqueous suspension, polymerizing a plurality of mer units of a hydrophilic monomer having a hydrophobic protection group, thereby forming a polymeric particle including a plurality of the hydrophobic protection groups. The method further includes converting the polymeric particle to a hydrophilic particle.
摘要:
Process for the preparation of beads of expandable vinyl aromatic polymers by means of polymerization in aqueous suspension, which comprises polymerizing at least one vinyl aromatic monomer in aqueous suspension in the presence of a peroxide initiator system, active at a temperature higher than 800 C, an expanding agent, and in the presence of: —an amide having the general formula R1CONHCH2—CH2NHCOR2 (I) a flame retardant system comprising a brominated additive with a bromine content higher than 30% by weight.
摘要:
A process for the preparation of expandable polystyrene including the following steps: i°) heating an aqueous suspension including styrene monomer and at least one organic peroxide initiator of formula (I) 1-alkoxy-1-t-alkylperoxycyclohexane in which the alkoxy group contains 1 to 4 carbon atoms, the t-alkyl group contains 4 to 12 carbon atoms, and the cyclohexane ring may optionally be substituted with 1 to 3 alkyl groups each, independently having 1 to 3 carbon atoms, at a temperature ranging from 100° C. to 120° C.), ii°) adding a blowing agent selected from the group of alkanes having from 4 to 6 carbon atoms and mixtures thereof. Also, an expandable polystyrene obtainable according to such a process and to insulation parts and packaging including such an expandable polystyrene.