摘要:
A coating method is disclosed including disposing a coating composition into a fluidly communicating space defined by an internal surface of an article. The fluidly communicating space includes at least one aperture, which is sealed, forming an enclosed space. The internal surface and the coating composition are heated under autogenous pressure, coating the internal surface with the coating composition. The at least one aperture is unsealed, re-forming the fluidly communicating space. Another coating method is disclosed in which the coating composition is disposed into a reservoir which is connected in fluid communication with the enclosed space prior to heating under autogenous pressure, coating the internal surface with the coating composition. Yet another coating method is disclosed in which the coating composition and the article are disposed in a vessel, which is sealed, forming the enclosed space prior to heating under autogenous pressure, coating the internal surface with the coating composition.
摘要:
The invention provides a process for forming crack-free dielectric films on a substrate. The process comprises the application of a dielectric precursor layer of a thickness from about 0.3 μm to about 1.0 μm to a substrate. The deposition is followed by low temperature heat pretreatment, prepyrolysis, pyrolysis and crystallization step for each layer. The deposition, heat pretreatment, prepyrolysis, pyrolysis and crystallization are repeated until the dielectric film forms an overall thickness of from about 1.5 μm to about 20.0 μm and providing a final crystallization treatment to form a thick dielectric film. The process provides a thick crack-free dielectric film on a substrate, the dielectric forming a dense thick crack-free dielectric having an overall dielectric thickness of from about 1.5 μm to about 20.0 μm.
摘要:
Provided is a coating liquid for forming a piezoelectric thin film containing lead zirconate titanate, the coating liquid including a complex precursor containing at least three kinds of metal elements of Pb, Ti, and Zr, the coating liquid being free from an exothermic peak at a temperature of 450° C. or more, or having a heat generation amount at a temperature of from 400° C. to 450° C., which is larger than a heat generation amount at a temperature of from 450° C. to 500° C., in differential thermal analysis of the coating liquid.
摘要:
A method for producing a layer for coating the inner surface of a container and a glass or plastic container obtained by said method, wherein said container is suitable for containing products biocompatible with humans and/or animals. The method includes: forming a solution containing a solvent, water, a molecular precursor comprising alkoxy groups and an acid as a catalyst, mixing said solution to initiate hydrolysis and condensation, applying the resulting solution onto at least one portion of the inner surface of the container, while the solution is in the process of gelling, the resulting applied solution is then dried at a temperature for a predetermined time, before curing. The acid is citric acid, wherein said citric acid is at a concentration of less than 6 mol/l, and in that the solution comprises less than 1.5 units of precursor for each volume unit of acid.
摘要:
A sol-gel method for forming durable, scratch-resistant coatings on glass substrates. Zirconia coatings, for example, are formed from a solution of zirconium oxychloride octahydrate in an organic, polar, aprotic solvent such as dimethylformamide. Annealed coatings, which optionally include an additive such as graphene, have a low coefficient of friction and can exhibit high hardness and hydrophobicity.
摘要:
A coating process comprising applying to a surface a coating composition consisting essentially of an alkali metal silicate and an aqueous liquid phase having dispersed therein solid aluminum particles to form on the surface a wet coating; and drying said wet coating: under conditions which convert said wet coating to an electrically conductive, corrosion-resistant, solid coating; or under conditions which form a solid coating which is not electrically conductive (non-conductive) and thereafter treating said non-conductive coating under conditions which convert said non-conductive coating to an electrically conductive, corrosion-resistant coating.
摘要:
An inorganic coating solution composition including an alkali metal silicate, a curing agent, a dispersant, a defoamer, and a solvent, wherein the curing agent is phosphoric acid (H2PO4), the dispersant is at least one selected from among Tween 20, Tween 40, Tween 60, Tween 80, polyvinyl pyrrolidone, polyethylene glycol 400 and polyvinyl alcohol, and the defoamer is at least one selected from among a silicone-based defoamer, an alcohol-based defoamer, a mineral oil-based defoamer and a powder defoamer.
摘要:
Embodiments of the present invention describe a method for continuous manufacture of a gel material comprising the steps of: forming a gel sheet by dispensing a gel precursor mixture onto a moving element at a rate effective to allow gelation to occur to the gel precursor mixture on the moving element; and cooling the formed gel thereby reducing the rate of solvent evaporation therefrom.
摘要:
Processes for forming metal oxide films on substrates are disclosed. The processes include depositing a composition comprising a metal oxide precursor, an amino acid, and a solvent onto a substrate. The composition is dried to remove solvent, and then heated to initiate combustion to form a metal oxide film.