摘要:
A method of making a coating solution includes the steps of polymerising an initial monomer feed comprising an N-vinyl pyrrolidone and an acrylate, preferably methacrylate, salt in water to synthesise a copolymer thereof, acidifying the resulting copolymer-water mixture to give free carboxylic acid groups along the copolymer backbone, diluting the aqueous solution down with alcohol, and adding a cross-linking agent which is capable of reacting with the carboxylic acid groups and curing the copolymer at a later stage after the coating solution has been applied to a substrate and the copolymer coated thereon. Also disclosed are a coating solution in storage, a method of coating a substrate which is on, or is part of, a medical device or other article, a substrate, article or medical device having a coating so applied, and a coated medical device packaged in a hydration solution. The aqueous-alcoholic coating solution may be stored for an extended period, suitably for at least one month and desirably for substantially longer, without deteriorating.
摘要:
The invention relates to a chain guide, respectively a chain tensioner for use in a lubricated sliding system, comprising a surface layer or bearing or comprising a sliding element comprising a surface layer, the surface layer being mainly made of a polymeric material containing a matrix polymer and optionally other components dispersed in said matrix polymer, wherein the matrix polymer consists of a semi-crystalline polyamide (SCPA) having a tensile modulus at 140° C. of at least 800 MPa (measured by the method according to ISO 527-1A). The invention also relates to a power train drive system comprising an engine, a transmission differential and a drive shaft system, a drive chain and a plastic component comprising a sliding element in contact with the lubricated drive chain, wherein the chain guide, the chain tensioner, respectively the sliding element has a coefficient of friction (CoF), measured in lubrication oil at 140° C. at a nominal contact pressure of 1 MPa and a speed of 1 m/s, of at most 0.07.
摘要:
The invention relates to a chain guide, respectively a chain tensioner for use in a lubricated sliding system, comprising a surface layer or bearing or comprising a sliding element comprising a surface layer, the surface layer being mainly made of a polymeric material containing a matrix polymer and optionally other components dispersed in said matrix polymer, wherein the matrix polymer consists of a semi-crystalline polyamide (SCPA) having a tensile modulus at 140° C. of at least 800 MPa (measured by the method according to ISO 527-1A). The invention also relates to a power train drive system comprising an engine, a transmission differential and a drive shaft system, a drive chain and a plastic component comprising a sliding element in contact with the lubricated drive chain, wherein the chain guide, the chain tensioner, respectively the sliding element has a coefficient of friction (Co F), measured in lubrication oil at 140° C. at a nominal contact pressure of 1 MPa and a speed of 1 m/s, of at most 0.07.
摘要:
An automotive engine oil and/or fuel comprising a base stock and an organic polymeric friction reducing additive is claimed. A method of reducing friction in an automotive engine oil and/or fuel by the addition of the organic polymeric friction reducing additive to the base stock is also claimed.
摘要:
The invention relates to the use of a polyamide prepared from at least one diamine and at least one dicarboxylic acid in a formulation for defoaming aqueous media. The invention also relates to defoamers for aqueous media that comprise such a polyamide.
摘要:
The present invention is directed to a dispersant additive comprising at least one adduct of (A) a polyolefin of 300 to 10,000 number average molecular weight substituted with at least 0.5 (e.g., from about 1 to 4) monocarboxylic acid producing moieties (preferably acid or ester moieties) per polyolefin molecule, (B) an amino-amine or thioamide-amine characterized by being a reaction product of at least a polyamine and an alpha, beta-unsaturated compound of the formula: ##STR1## wherein X is sulfur or oxygen, Y is --OR.sup.4, --SR.sup.4, or --NR.sup.4 (R.sup.5), and R.sup.1, R.sup.2, R.sup.3, R.sup.4 and R.sup.5 are the same or different and are hydrogen or substituted or unsubstituted hydrocarbyl.
摘要:
Provided is a lubricating oil composition for a transmission having excellent gear properties, clutch properties, cooling properties, and electric insulating properties. The lubricating oil composition for a transmission preparing by blending (A) a base oil, (B) a viscosity index improver having a mass average molecular weight of 10,000 to 50,000, and (C-1) a polyamide and/or (C-2) a polyol ester, the base oil (A) including (A-1) a synthetic oil having a kinematic viscosity at 100° C. of 1.0 to 10.0 mm2/s.
摘要:
Provided herein are copolymers of a polyaminopolymer and polyanhydride, wherein the polyaminopolymer comprises a polyaminopolyolefin; and methods of their preparation.
摘要:
A coating composition comprises: (a) a resin solution containing a polyamide-imide resin and a solvent having a urea bond; and (b) a powdered solid lubricant. In general, the coating composition containing a polyamide-imide resin does not raise any concern about reproductive toxicity and has excellent lubrication durability.
摘要:
Provided herein are copolymers of a polyaminopolymer and polyanhydride, wherein the polyaminopolymer comprises a polyaminopolyolefin; and methods of their preparation.