摘要:
The invention relates to a coated body and to a method for coating a body. The coated body comprises at least a substrate (22), a diamond layer (24) having a thickness of 1-40 μm, and a hard material layer (26), which is arranged farther outside on the body (10) than the diamond layer (24). The hard material layer (26) comprises at least one metal element and at least one non-metal element. An adhesive layer (32) having a thickness of 2-80 nm is provided between the diamond layer (24) and the hard material layer (26). The adhesive layer (32) contains carbon and at least one metal element. The diamond layer (24) can be applied by means of a CVD method. The hard material layer can be applied by means of a PVD method. The adhesive layer (32) between the diamond layer (24) and the hard material layer (26) can be produced in that, before the hard material layer (26) is applied, the surface of the diamond layer (24) is pretreated by means of HIPIMS metal ion etching, wherein ions are implanted into or diffuse into the surface of the diamond layer (24) by means of metal ion etching.
摘要:
A surface-coated titanium carbonitride-based cermet cutting tool is a surface-coated TiCN-based cermet cutting tool in which a Ti compound layer that is a hard coating layer is deposited as a first layer on the surface of a TiCN-based cermet body containing W and Mo, and a Mo-enriched layer having an average thickness of 0.5 to 10 nm is formed at an interface between a TiCN phase of the body and the hard coating layer.
摘要:
Provided is a jewelry ring comprising a substrate, a first coating of a metallic nitride or a metallic boride, and an external metallic coating. Also provided is a metallic article comprising a substrate comprising tungsten carbide, cobalt, tungsten, titanium, titanium carbide, zirconium, tantalum or aluminum; a first coating of a metallic nitride or a metallic boride; and an external metallic coating. A method for making a jewelry ring comprising a substrate, a first coating of a metallic nitride or a metallic boride, and an external metallic coating is additionally provided. Further provided is a method for making a metallic article comprising a substrate comprising tungsten carbide, cobalt, tungsten, titanium, titanium carbide, zirconium, tantalum or aluminum; a first coating of a metallic nitride or a metallic boride; and an external metallic coating.
摘要:
The invention relates to a coating comprising at least one molybdenum-containing layer having molybdenum oxide, said molybdenum being essentially molybdenum monoxide. The invention further relates to a PVD process for producing the disclosed coating, in which the layer comprising the molybdenum monoxide is produced using arc evaporation. The invention also relates to a component that has said coating.
摘要:
A sliding member includes: a base; a chromium-based hard chromium plated layer formed on the surface of the base; a hard carbon layer that is mainly composed of carbon element and is formed on the hard chromium plated layer. The hydrogen concentration of the hard chromium plated layer is equal to or less than 150 mass ppm. A method for producing the sliding member involves heating the surface of the base on which the chromium-based hard chromium plated layer has been formed at a temperature of 250° C. or more so that the hydrogen concentration of the hard chromium plated layer is equal to or less than 150 mass ppm, and thereafter forming the hard carbon layer mainly composed of carbon element on the hard chromium plated layer.
摘要:
Provided are low friction coatings with improved abrasion, wear resistance and methods of making such coatings. In one form, the coating includes: i) an under layer selected from the group consisting of CrN, TiN, TiAlN, TiAlVN, TiAlVCN, TiSiN, TiSiCN, TiAlSiN and combinations thereof, wherein the under layer ranges in thickness from 0.1 to 100 μm, ii) an adhesion promoting layer selected from the group consisting of Cr, Ti, Si, W, CrC, TiC, SiC, WC, and combinations thereof, wherein the adhesion promoting layer ranges in thickness from 0.1 to 50 μm and is contiguous with a surface of the under layer, and iii) a functional layer selected from the group consisting of a fullerene based composite, a diamond based material, diamond-like-carbon and combinations thereof, wherein the functional layer ranges from 0.1 to 50 μm and is contiguous with a surface of the adhesion promoting layer.
摘要:
The thermal barrier coating system comprises a matrix of a first chemistry with multiple embedded second phases of a second chemistry. The matrix comprises a stabilized zirconia. The second regions comprise at least 40 mole percent of oxides having the formula Ln2O3, where Ln is selected from the lanthanides La through Lu, Y, Sc, In, Ca, and Mg with the balance zirconia (ZrO2), hafnia (HfO2), titania (TiO2), or mixtures thereof. The second phases have a characteristic thickness (T6) of less than 2.0 micrometers (μm). The spacing between second phases has a characteristic thickness (T5) of less than 8.0 micrometers (μm).
摘要:
Tool with optional wear-protection coating has, as an outer layer arranged on top of the substrate body or wear-protection coating, a single-layer wear-recognition layer (A) or a multilayer wear-recognition layer (B) comprising at least 4 individual layers arranged one above another, said layer or layers being produced by depositing elemental metals, metal alloys or electrically conductive metal compounds with a PVD process. Individual layer of (A) or at least one individual layer of (B) contain at least two different metals, the wear-recognition layer comprises a region produced by anodic oxidation from the upper surface down to a penetration depth that does not extend over the entire thickness of the wear-recognition layer, and the individual layer of (A) or the at least one individual layer of (B) has at least two different phases before the anodic oxidation and in the regions of the wear recognition layer that are not anodically oxidized.
摘要:
A golf club component, such as a golf club head and/or a golf club shaft, can comprise a golf club component substrate having an outer layer of titanium carbide, typically comprising at least forty percent (40%) carbon content. Alternatively, a golf club component can comprise a golf club component substrate, at least a portion of which is enveloped by a first coating layer of, for example, electroplated nickel, a second coating layer of, for example, electroplated chromium or palladium, and a third coating layer of titanium carbide applied by physical vapor deposition. The titanium carbide layer is durable and can provide the golf club component with a desired aesthetic appearance, such as a black color. Additionally, the golf club component can be coated with a fourth coating layer, such as a layer comprising a sealant or clear coat material.
摘要:
A coating on mono- or poly-crystalline diamond or diamond-containing material includes a first adhesive layer formed directly on the diamond or diamond-containing material, the first layer including tungsten and tungsten carbide alloyed with fluorine in an amount of 0.001 to 0.12 wt % calculated on the total weight of the first layer. The coating further includes a second protective layer formed on the first layer, the second layer including at least tungsten alloyed with fluorine in an amount of 0.001 to 0.12 wt % calculated on the total weight of the second layer. The adhesive layer provides excellent bond strength to diamond, while the protective layer provides good protection against oxidation and molten metals used for attaching the coated diamonds to tools.