摘要:
An inorganic board contains, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml. Also, a method includes: step of producing a slurry containing hydraulic material, reinforcing fiber, and wollastonite; step of producing a sheet by dehydrating the slurry; and step of pressing and curing the sheet; wherein, in the step of producing a slurry, a composition of the slurry is set so as to contain, in a solid content ratio, 30 to 70 mass % of hydraulic material, 5 to 15 mass % of reinforcing fiber, and 1 to 30 mass % of wollastonite having a wet volume (after being allowed to stand for 30 minutes) of 15 to 45 ml.
摘要:
A hydraulic composition includingfrom 220 to 500 kg per cubic metre of fresh hydraulic composition, of a hydraulic binder including Portland cement;from 400 to 1200 kg per cubic metre of the fresh hydraulic composition, of a sand having a D10 greater than 0.1 mm and a D90 less than 6 mm;from 0.1 to 5 % by mass of dry extract relative to the mass of the hydraulic binder of a retarding agent;from 0.05 to 5 % by mass of dry extract relative to the mass of the hydraulic binder of a superplasticizer; andfrom 0.01 to 2% by mass of dry extract relative to the mass of the hydraulic binder of a rheology-modifying agent.
摘要:
The invention relates to compressed blocks of wood agglomerate, comprising wood particles and a hydraulic binder, produced by a method in which an initial mixture comprising wood particles and a hydraulic binder is held under pressure for the duration of the hardening of the binder. The invention further relates to a method for production of said blocks and the use thereof in particular, as construction elements for buildings.
摘要:
A process for preparing a zeolite-based monolith including dry-mixing zeolite particles and a temporary binder until homogenization; adding silica and water dispersion; wet-kneading and high-shear mixing until obtaining a homogenous pulp; extrusion-molding the pulp resulting from the previous step; controlled drying of the mold obtained; and oxidizing at a high temperature to obtain the monolith.
摘要:
Compositions, methods, and systems for manufacturing articles, particularlycontainers and packaging materials, having a particle packed, highly inorganically filled, cellular matrix are disclosed. Suitable inorganically filled mixtures are prepared by mixing together a starch-based binder, a solvent, inorganic aggregates, and optimal admixtures, e.g., fibers, mold-releasing agents, rheology-modifying agents, plasticizers, coating materials, and dispersants, in the correct proportions to form an article which has the desired performance criteria. The inorganically filled mixtures have a predetermined viscosity and are heated between molds at an elevated temperature and pressure to produce form-stable articles having a desired shape and a selectively controlled cellular, structural matrix. The molded articles may be placed in a high humidity chamber to obtain the necessary flexibility for their intended use. The articles may be manufactured to have properties substantially similar to articles presently made from conventional materials like paper, paperboard, polystyrene, plastic, or other organic materials. They have especial utility in the mass-production of containers, particularly food and beverage containers.
摘要:
Compositions, methods, and systems for manufacturing articles, particularly containers and packaging materials, having a particle packed, highly inorganically filled, cellular matrix are disclosed. Suitable inorganically filled mixtures are prepared by mixing together a starch-based binder, a solvent, inorganic aggregates, and optimal admixtures, e.g., fibers, mold-releasing agents, rheology-modifying agents, plasticizers, coating materials, and dispersants, in the correct proportions to form an article which has the desired performance criteria. The inorganically filled mixtures have a predetermined viscosity and are heated between molds at an elevated temperature and pressure to produce form-stable articles having a desired shape and a selectively controlled cellular, structure matrix. The molded articles may be placed in a high humidity chamber to obtain the necessary flexibility for their intended use. The articles may be manufactured to have properties substantially similar to articles presently made from conventional materials like paper, paperboard, polystyrene, plastic, or other organic materials. They have especial utility in the mass-production of containers, particularly food and beverage containers.
摘要:
Compositions, methods, and systems for manufacturing articles, particularly containers and packaging materials, having a highly inorganically filled matrix. Suitable inorganically filled mixtures are prepared by mixing together an organic polymer binder, water, one or more aggregate materials, fibers, and optional admixtures in the correct proportions in order to form an article which has the desired performance criteria. The inorganically filled mixtures are molded to fashion a portion of the mixture into a form stable shape for the desired article. Once the article has obtained form stability, the article is removed from the mold and allowed to harden to gain strength. The articles may have properties substantially similar to articles presently made from traditional materials like paper, paperboard, polystyrene, plastic, or metal. They have especial utility in the mass production of containers, particularly food and beverage containers.
摘要:
Compositions, methods, and systems for manufacturing articles, particularly containers and packaging materials, having a fiber-reinforced, starch-bound cellular matrix. Suitable mixtures used to form the articles are prepared by first preparing a viscous preblended mixture comprising water, a gelatinized starch-based binder, and fibers having an average length greater than about 2 mm. The highly viscous preblended mixture effectively transfers the shearing forces of the mixer to the fibers. The final moldable mixture is then prepared by mixing into the preblended mixture the remaining starch-based binder, water, and other desired admixtures, e.g., mold-releasing agents, inorganic filler rheology-modifying agents, plasticizers, coating materials, and dispersants, in the correct proportions to form an article which has the desired performance criteria. The moldable mixtures are heated between molds at an elevated temperature and pressure to produce form-stable articles having a desired shape and a selectively controlled foamed structural matrix. The articles may be manufactured to have properties substantially similar to articles presently made from conventional materials like paper, paperboard, polystyrene, plastic, or other organic-based materials and have especial utility in the mass-production of containers, particularly food and beverage containers.
摘要:
Cementitious containers which have a cementitious structural matrix for use in the packaging, storing, partitioning, and/or shipping of goods. The containers are manufactured from cementitious materials in order to be strong, durable, tough, lightweight, cushioning, insulative, inexpensive, and more environmentally compatible than those currently used in packaging, storing, and/or shipping goods. The cementitious structural matrix of the containers includes a hydraulic cement paste (formed from the reaction of water with, e.g., a portland cement) in combination with a rheology-modifying plasticizer, such as methylhydroxyethylcellulose. Preferred embodiments may also include various aggregate materials, fibrous materials, and air voids, which add the necessary strength while making the product lightweight, and which can provide insulative properties (if desired) at a cost which is economically justified in comparison to conventional paper and polystyrene products. The molded cementitious mixtures generally have sufficient strength in the green (or uncured) state to maintain their molded shape. The cementitious mixtures can be formed into flat sheets having greatly varying thicknesses depending upon the intended use of the container. Corrugated sheets can be made to increase the container strength.
摘要:
Processes disclosed are capable of converting biomass into high-crystallinity, hydrophobic cellulose. In some variations, the process includes fractionating biomass with an acid (such as sulfur dioxide), a solvent (such as ethanol), and water, to generate cellulose-rich solids and a liquid containing hemicellulose and lignin; and depositing lignin onto cellulose fibers to produce lignin-coated cellulose materials (such as dissolving pulp). The crystallinity of the cellulose material may be 80% or higher, translating into good reinforcing properties for composites. Optionally, sugars derived from amorphous cellulose and hemicellulose may be separately fermented, such as to monomers for various polymers. These polymers may be combined with the hydrophobic cellulose to form completely renewable composites.